PC Makrolon®  9417C 012124 COVESTRO SHANGHAI

215
  • Unit Price:US$ 3,413 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardanttransparentFiller: Glass fiber reinforced material10% filler by weight10% filler by weight
  • Application Areas:Automotive components
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°C,Complete BreakISO 179/1eU120 kJ/m²
Multi axis Instrumented Impact Energy-30°CISO 6603-215.0 J
Impact strength of cantilever beam gap23°C,CompleteBreakISO 739110 kJ/m²
Impact strength of simply supported beam without notch23°C,Complete BreakISO 179/1eU150 kJ/m²
Impact strength of simply supported beam without notch-60°C,CompleteBreakISO 179/1eU100 kJ/m²
Charpy Notched Impact Strength23°C,CompleteBreakISO 739110 kJ/m²
Multi axis Instrumented Impact Energy23°CISO 6603-225.0 J
Multi axis Instrumented Peak Impact Force23°CISO 6603-24000 N
Multi axis Instrumented Peak Impact Force-30°CISO 6603-23700 N
flammabilityTest ConditionTest MethodTest Result
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
Hot filament ignition temperature1.5mmIEC 60695-2-13900 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13900 °C
Extreme Oxygen IndexISO 4589-235 %
Burning rate - US-FMVSS>1.00mmISO 3795passed
ApplicationofFlamefromSmallBurner MethodKandF2.00mmDIN 53438-1,-3K1.F1
FlashIgnitionTemperatureASTM D1929470 °C
SelfIgnitionASTM D1929550 °C
Burning wire flammability index1.5mmIEC 60695-2-12960 °C
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
Burning wire flammability index0.75mmIEC 60695-2-12960 °C
UL flame retardant rating6.0mmUL 945VA
UL flame retardant rating3.0mmUL 945VA
UL flame retardant rating1.5mmUL 94V-0
mechanical propertiesTest ConditionTest MethodTest Result
Bending strain23°CISO 1785.8 %
bending strength23°CISO 178105 Mpa
bending strength3.5%Strain,23°CISO 17895.0 Mpa
Bending modulus23°CISO 1783600 Mpa
Tensile modulus23°CISO 527-2/13800 Mpa
tensile strengthYield,23°CISO 527-2/564.0 Mpa
tensile strengthBreak,23°CISO 527-2/545.0 Mpa
Tensile strainYield,23°CISO 527-2/54.6 %
Tensile strainBreak,23°CISO 527-2/515 %
Tensile creep modulus1000hrISO 899-12900 Mpa
Tensile creep modulus1hrISO 899-13600 Mpa
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionTD:23to55°CISO 11359-26.5E-05 cm/cm/°C
RTI Str1.5mmUL 746125 °C
RTI Imp1.5mmUL 746115 °C
thermal conductivity23°CISO 83020.22 W/m/K
RTI Elec1.5mmUL 746125 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B141 °C
Vicat softening temperature--ISO 306/B50143 °C
Vicat softening temperature--ISO 306/B120144 °C
Ball Pressure Test136°CIEC 60695-10-2Pass
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A135 °C
Linear coefficient of thermal expansionMD:23to55°CISO 11359-24E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateTD:2.00mm3ISO 294-40.45 %
Shrinkage rateMDISO 25770.40-0.60 %
Shrinkage rateTDISO 25770.40-0.60 %
melt mass-flow rate300°C/1.2kgISO 11337.0 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11336.00 cm3/10min
Water absorption rateEquilibrium,23°C,50%RHISO 620.10 %
density23°CISO 11831.27 g/cm³
Apparent densityISO 600.64 g/cm³
Shrinkage rateMD:2.00mm3ISO 294-40.60 %
Water absorption rateSaturation,23°CISO 620.26 %
Electrical performanceTest ConditionTest MethodTest Result
Relative permittivity23°C,1MHzIEC 602503.20
Relative permittivity23°C,100HzIEC 602503.20
Dielectric strength23°C,1.00mmIEC 60243-136 KV/mm
Volume resistivity23°CIEC 600931E+16 ohms·cm
Surface resistivityIEC 600931E+16 ohms
Compared to the anti leakage trace indexSolutionBIEC 60112PLC 4
Compared to the anti leakage trace indexSolutionAIEC 60112PLC 3
Dissipation factor23°C,100HzIEC 602501E-03
Dissipation factor23°C,1MHzIEC 602509E-03
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1128 Mpa
Supplementary InformationTest ConditionTest MethodTest Result
Electrolytic corrosion23°CIEC 60426A1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.