Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 9417C 012124 COVESTRO SHANGHAI
Makrolon®
Automotive components
Flame retardant、transparent、Filler: Glass fiber reinf、10% filler by weight、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| CharpyNotchedImpactStrength6 | 23°C,CompleteBreak | ISO7391 | 10 kJ/m² |
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 25.0 J |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 3700 N |
| Impact strength of simply supported beam without notch | -60°C,CompleteBreak | ISO179/1eU | 100 kJ/m² |
| -30°C,完全断裂 | ISO179/1eU | 120 kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 15.0 J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO6603-2 | 4000 N |
| NotchedIzodImpactStrength7 | 23°C,CompleteBreak | ISO7391 | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C,完全断裂 | ISO179/1eU | 150 kJ/m² |
| hardness | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| ISO2039-1 | 128 Mpa |
| Supplementary Information | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 |
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| Bending stress | 3.5%Strain,23°C | ISO178 | 95.0 Mpa |
| 23°C | ISO178 | 105 Mpa | |
| Flexural modulus | 23°C | ISO178 | 3600 Mpa |
| 23°C | ISO178 | 5.8 % | |
| TensileCreepModule | 1hr | ISO899-1 | 3600 Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/5 | 4.6 % |
| Tensile stress | 屈服,23°C | ISO527-2/5 | 64.0 Mpa |
| Tensile strain | 断裂,23°C | ISO527-2/5 | 15 % |
| Tensile stress | 断裂,23°C | ISO527-2/5 | 45.0 Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 3800 Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 2900 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| Volume resistivity | 23°C | IEC60093 | 1E+16 ohms·cm |
| Surface Resistivity | IEC60093 | 1E+16 ohms | |
| CTI | 解决方案A | IEC60112 | 175 V |
| 解决方案B | IEC60112 | 125 V | |
| dielectric strength | 23°C,1.00mm | IEC60243-1 | 36 KV/mm |
| Dissipation Factor | 23°C,1MHz | IEC60250 | 9E-03 |
| 23°C,1MHz | IEC60250 | 3.20 | |
| Dissipation Factor | 23°C,100Hz | IEC60250 | 1E-03 |
| 23°C,100Hz | IEC60250 | 3.20 |
| flammability | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| Extreme Oxygen Index 9 | ISO4589-2 | 35 % | |
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 900 °C |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 960 °C |
| SelfIgnitionTemperature | ASTMD1929 | 550 °C | |
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| 1.5mm | IEC60695-2-13 | 900 °C | |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 °C |
| FlashIgnitionTemperature | ASTMD1929 | 470 °C | |
| >1.00mm | ISO3795 | passed | |
| ApplicationofFlamefromSmallBurner-Method | 2.00mm | DIN53438-1,-3 | K1,F1 |
| UL flame retardant rating | 1.5mm | UL94 | V-0 |
| 3.0mm,NC,BK,GY | UL94 | 5VA | |
| 6.0mm | UL94 | 5VA |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm3 | ISO294-4 | 0.60 % |
| TD | ISO2577 | 0.40to0.60 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.10 % |
| density | 23°C | ISO1183 | 1.27 g/cm³ |
| Water absorption rate | 饱和,23°C | ISO62 | 0.26 % |
| Shrinkage rate | TD:2.00mm3 | ISO294-4 | 0.45 % |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 6.00 cm3/10min |
| Apparent density 2 | ISO60 | 0.64 g/cm³ | |
| Shrinkage rate | MD | ISO2577 | 0.40to0.60 % |
| melt mass-flow rate | 300°C/1.2kg | ISO1133 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/9417C 012124 |
|---|---|---|---|
| Thermal conductivity coefficient 8 | 23°C | ISO8302 | 0.22 W/m/K |
| RTI Elec | 1.5mm | UL746 | 125 °C |
| 0.45MPa,未退火 | ISO75-2/B | 141 °C | |
| RTI Str | 1.5mm | UL746 | 125 °C |
| 1.8MPa,未退火 | ISO75-2/A | 135 °C | |
| RTI Imp | 1.5mm | UL746 | 115 °C |
| BallPressure Test | 136°C | IEC60695-10-2 | Pass |
| vicat | -- | ISO306/B50 | 143 °C |
| -- | ISO306/B120 | 144 °C | |
| TD：23to55°C | ISO11359-2 | 6.5E-05 cm/cm/°C | |
| MD：23到55°C | ISO11359-2 | 4E-05 cm/cm/°C |