PC EMERGE™ 8701-15 STYRON TAIWAN

206

Unit Price:US$ 4,061 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Glass fiber reinforced｜enhance
Application Areas:Instrumentation｜Video devices｜component
Color:--
Grade:Enhanced level

Technical Data Sheet

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	141 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	133 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	139 °C
Vicat softening temperature	--	ISO 306/A120	155 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145 °C
Ball pressure temperature		IEC 60335-1	>130 °C
Linear coefficient of thermal expansion	MD：-40to80°C	ASTM D696	1.5E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	960 °C
	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	960 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	960 °C
Extreme Oxygen Index		ISO 4589-2	29 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity	2.00mm	IEC 60093	1E+16 ohms·cm
Dielectric strength	2.00mm	IEC 60243-1	>70 KV/mm
Dielectric constant	2.00mm,50Hz	IEC 60250	3.00
Dielectric constant	Dielectric constant	2.00mm,1MHz	IEC 60250	3.10
Dissipation factor	2.00mm,50Hz	IEC 60250	8E-03
Dissipation factor	Dissipation factor	2.00mm,1MHz	IEC 60250	0.016
Compared to the anti leakage trace index	3.00mm,SolutionA	IEC 60112	PLC 3

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ISO 294-4	0.40-0.60 %
melt mass-flow rate	300°C/1.2kg	ISO 1133	15 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	4.00mm,InjectionMolded	ISO 527-2/1	3950 Mpa
Tensile modulus	Tensile modulus	4.00mm,InjectionMolded	ISO 527-2/50	4000 Mpa
tensile strength	Yield,4.00mm,InjectionMolded	ISO 527-2/50	65.0 Mpa
tensile strength	tensile strength	Break,4.00mm,Injection	ISO 527-2/50	50.0 Mpa
Tensile strain	Yield,4.00mm,InjectionMolded	ISO 527-2/50	4.0 %
Tensile strain	Tensile strain	Break,4.00mm,Injection	ISO 527-2/50	9.0 %
Bending modulus	4.00mm,InjectionMolded	ISO 178	3800 Mpa
bending strength	4.00mm,InjectionMolded	ISO 178	105 Mpa

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,InjectionMolded	ISO 180/A	9.0 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.