PC 8701-15 STYRON TAIWAN
EMERGE™
Instrumentation、Video devices、component
Flame retardant、Glass fiber reinforced、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | STYRON TAIWAN/8701-15 |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C,InjectionMolded | ISO 180/A | 9.0 kJ/m² |
Electrical performance | Test Condition | Test Method | STYRON TAIWAN/8701-15 |
---|---|---|---|
dielectric constant | 2.00mm,50Hz | IEC 60250 | 3.00 |
dielectric strength | 2.00mm | IEC 60243-1 | >70 KV/mm |
dielectric constant | 2.00mm,1MHz | IEC 60250 | 3.10 |
Compared to the Leakage Tracking Index (CTI) | 3.00mm,SolutionA | IEC 60112 | PLC 3 |
Surface Resistivity | IEC 60093 | 1E+14 ohms | |
Volume resistivity | 2.00mm | IEC 60093 | 1E+16 ohms·cm |
Dissipation Factor | 2.00mm,50Hz | IEC 60250 | 8E-03 |
2.00mm,1MHz | IEC 60250 | 0.016 |
Mechanical properties | Test Condition | Test Method | STYRON TAIWAN/8701-15 |
---|---|---|---|
Flexural modulus | 4.00mm,InjectionMolded | ISO 178 | 3800 Mpa |
bending strength | 4.00mm,InjectionMolded | ISO 178 | 105 Mpa |
tensile strength | Yield,4.00mm,InjectionMolded | ISO 527-2/50 | 65.0 Mpa |
断裂,4.00mm,注塑 | ISO 527-2/50 | 50.0 Mpa | |
Tensile strain | Yield,4.00mm,InjectionMolded | ISO 527-2/50 | 4.0 % |
Tensile modulus | 4.00mm,InjectionMolded | ISO 527-2/1 | 3950 Mpa |
Tensile strain | 断裂,4.00mm,注塑 | ISO 527-2/50 | 9.0 % |
Tensile modulus | 4.00mm,InjectionMolded | ISO 527-2/50 | 4000 Mpa |
flammability | Test Condition | Test Method | STYRON TAIWAN/8701-15 |
---|---|---|---|
Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 960 °C |
3.0mm | IEC 60695-2-13 | 960 °C | |
1.0mm | IEC 60695-2-13 | 960 °C | |
UL flame retardant rating | 1.5mm | UL 94 | V-0 |
Limiting Oxygen Index | ISO 4589-2 | 29 % |
physical property | Test Condition | Test Method | STYRON TAIWAN/8701-15 |
---|---|---|---|
Shrinkage rate | MD | ISO 294-4 | 0.40-0.60 % |
melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 15 g/10min |
Thermal performance | Test Condition | Test Method | STYRON TAIWAN/8701-15 |
---|---|---|---|
Ball pressure temperature | IEC 60335-1 | >130 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 141 °C |
vicat | -- | ISO 306/A120 | 155 °C |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 139 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 133 °C | |
vicat | -- | ISO 306/B50 | 145 °C |
Linear coefficient of thermal expansion | MD:-40到80°C | ASTM D696 | 1.5E-05 cm/cm/°C |