PA66 Durethan® AKV35 000000 ENVALIOR WUXI
185
- Unit Price:US$ 3,530 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:71MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Filler: Glass fiber reinforced material｜35% filler by weight
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD | ISO 11359-2 | 1E-04 cm/cm/°C | |
| Hot deformation temperature | 0.45MPaUnannealed | ISO 75-2/Bf | 250 °C |
| 1.80MPaAnnealed | ISO 75-2/Af | 250 °C | |
| Vicat softening temperature | Melting Temperature | ISO 11357-3 | 263 °C |
| flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.60mm | |
| UL -94 | HB 3.20mm | ||
| Extreme Oxygen Index | ISO 4589-2 | 23 % | |
| Ignition temperature of heating wire | 2.00mm | IEC 60695-2-12 | 600 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | MD3.0mm | ISO 294-4 | 0.32 % |
| TD3.0mm | ISO 294-4 | 1.40 % | |
| Water absorption rate | (23°C,50RH) | ISO 62 | 1.80 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm | |
| Surface resistivity | IEC 60093 | 1E+14 Ω.cm | |
| Dielectric strength | 1.00mm | IEC 60243-1 | 40 KV/mm |
| Dielectric constant | 23°C | IEC 60250 | 4.00 100HZ |
| 23°C | IEC 60250 | 4.00 1MHz | |
| 相对漏电起痕指数 | IEC 60112 | 600 V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 23°C | ISO 527-2 | 200 Mpa |
| Elongation at Break | 23°C | ISO 527-2 | 3.00 % |
| Tensile modulus | 23°C | ISO 527-2 | 11200 Mpa |
| bending strength | 23°C | ISO 178 | 300 Mpa |
| Bending modulus | 23°C | ISO 178 | 10000 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| -30°C | ISO 179/1eU | 75 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | <10 kJ/m² |
| -40°C | ISO 180/1A | <10 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.