PA66 AKV35 000000 ENVALIOR WUXI
Durethan®
--
Filler: Glass fiber reinf、35% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/AKV35 000000 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 90 kJ/m² |
| -30°C | ISO179/1eU | 75 kJ/m² | |
| Tensile modulus | 23°C | ISO527-2 | 11200 Mpa |
| Flexural modulus | 23°C | ISO178 | 10000 Mpa |
| elongation at break | 23°C | ISO527-2 | 3.00 % |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | <10 kJ/m² |
| -40°C | ISO180/1A | <10 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 15 kJ/m² |
| bending strength | 23°C | ISO178 | 300 Mpa |
| tensile strength | 23°C | ISO527-2 | 200 Mpa |
| Electrical performance | Test Condition | Test Method | ENVALIOR WUXI/AKV35 000000 |
|---|---|---|---|
| dielectric constant | 23°C | IEC60250 | 4.00 100HZ |
| 相对漏电起痕指数 | IEC60112 | 600 V | |
| IEC60093 | 1E+15 Ω.cm | ||
| dielectric constant | 23°C | IEC60250 | 4.00 1MHz |
| Surface Resistivity | IEC60093 | 1E+14 Ω.cm | |
| Dielectric Strength | 1.00mm | IEC60243-1 | 40 KV/mm |
| Flame retardant performance | Test Condition | Test Method | ENVALIOR WUXI/AKV35 000000 |
|---|---|---|---|
| fire rating | 氧指数 | ISO4589-2 | 23 % |
| GWIT | 2.00mm | IEC60695-2-12 | 600 °C |
| fire rating | UL-94 | 3.20mm HB |
| physical property | Test Condition | Test Method | ENVALIOR WUXI/AKV35 000000 |
|---|---|---|---|
| Water absorption rate | (23°C,50RH) | ISO62 | 1.80 % |
| Shrinkage rate | MD3.0mm | ISO294-4 | 0.32 % |
| TD3.0mm | ISO294-4 | 1.40 % |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/AKV35 000000 |
|---|---|---|---|
| TD | ISO11359-2 | 1E-04 cm/cm/°C | |
| 0.45MPa未退火 | ISO75-2/Bf | 250 °C | |
| 1.80MPa退火 | ISO75-2/Af | 250 °C | |
| MD | ISO11359-2 | 2E-05 cm/cm/°C | |
| vicat | 熔融温度 | ISO11357-3 | 263 °C |