Material Description

Material Properties:Glass fiber reinforced｜Flame retardant｜enhance
Application Areas:Automotive sector｜Electrical field｜Electronic field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2100 J/m
Reverse notch impact	3.20 mm	ASTM D256	2100 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	96.0 Mpa
elongation	Break	ASTM D638	70 %
Bending modulus	100 mm Span	ASTM D790	3170 Mpa
bending strength	Yield, 100 mm Span	ASTM D790	144 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			135 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			340 to 360 °C
Temperature in the middle of the barrel			345 to 365 °C
Temperature at the front of the material cylinder			350 to 370 °C
Spray nozzle temperature			350 to 370 °C
Processing (melt) temperature			350 to 370 °C
Mold temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	190 °C
RTI Elec		UL 746	115 °C
RTI Imp		UL 746	115 °C
RTI		UL 746	115 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	24 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %

Electrical performance	Test Method	Test Result
Compared to the anti leakage trace index	UL 746	PLC 4
High arc combustion index	UL 746	PLC 4
Hot wire ignition	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.