thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 6.40 mm	ASTM D648	260 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm	ASTM D648	220 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0 mm	UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	3.20 mm，Flow	ASTM D955	0.30 - 0.90 %

Electrical performance	Test Condition	Test Method	Test Result
dielectric strength	23°C, 1.00 mm	ASTM D149	35 KV/mm
Compared to the Leakage Tracking Index (CTI)	解决方案 A	IEC 60112	V

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 100 °C
drying time			3.0 to 5.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			270 to 290 °C
Temperature in the middle of the barrel			280 to 310 °C
Temperature at the front of the material cylinder			290 to 310 °C
Spray nozzle temperature			280 to 310 °C
Processing (melt) temperature			280 to 310 °C
mold temperature			80 to 150 °C
screw speed			40 to 80 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	断裂, 3.20 mm	ASTM D638	118 Mpa
elongation	断裂, 3.20 mm	ASTM D638	2.0 %
flexural modulus	3.20 mm	ASTM D790	8830 Mpa
bending strength	屈服, 3.20 mm	ASTM D790	177 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.