Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SPS SP2300 LG CHEM KOREA
LUSEP®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/SP2300 |
|---|---|---|---|
| bending strength | 屈服, 3.20 mm | ASTM D790 | 177 Mpa |
| tensile strength | 断裂, 3.20 mm | ASTM D638 | 118 Mpa |
| elongation | 断裂, 3.20 mm | ASTM D638 | 2.0 % |
| Flexural modulus | 3.20 mm | ASTM D790 | 8830 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/SP2300 |
|---|---|---|---|
| dielectric strength | 23°C, 1.00 mm | ASTM D149 | 35 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | V |
| flammability | Test Condition | Test Method | LG CHEM KOREA/SP2300 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LG CHEM KOREA/SP2300 |
|---|---|---|---|
| Shrinkage rate | 3.20 mm，Flow | ASTM D955 | 0.30 - 0.90 % |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/SP2300 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 220 °C |
| 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 260 °C |
| injection | Test Condition | Test Method | LG CHEM KOREA/SP2300 |
|---|---|---|---|
| drying time | 3.0 to 5.0 hr | ||
| screw speed | 40 to 80 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 280 to 310 °C | ||
| Temperature at the rear of the barrel | 270 to 290 °C | ||
| Processing (melt) temperature | 280 to 310 °C | ||
| drying temperature | 80 to 100 °C | ||
| Temperature at the front of the material cylinder | 290 to 310 °C | ||
| Temperature | 80 to 150 °C | ||
| Spray nozzle temperature | 280 to 310 °C |