PEEK KetaSpire® PEEK KT-820CF30 SOLVAY USA

291

Unit Price:US$ 86,371 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
17MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Carbon fiber reinforced material｜30% filler by weight
Application Areas:Solvay｜Solvie｜ Belgium
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Melt viscosity	400°C,1000sec^-1	ASTM D3835	920 Pa·s

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	--	ASTM D4812	750 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	--	ISO 180	44 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	0.8mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--4	ASTM D638	19700 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	22800 Mpa
tensile strength	Yield	ISO 527-2/1A/5	217 Mpa
tensile strength	tensile strength	--	ASTM D638	201 Mpa
elongation	Break4	ASTM D638	2.0 %
elongation	elongation	Break	ISO 527-2/1A/5	2.0 %
Bending modulus	--	ASTM D790	17500 Mpa
Bending modulus	Bending modulus	--	ISO 178	20500 Mpa
bending strength	--	ASTM D790	317 Mpa
bending strength	bending strength	--	ISO 178	311 Mpa
compressive strength		ASTM D695	173 Mpa
shear strength		ASTM D732	95.1 Mpa
Poisson's ratio			7.58 0.42

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	315 °C
Glass transition temperature		ASTM D3418	150 °C
Melting temperature		ASTM D3418	340 °C
Linear coefficient of thermal expansion	MD：-50to50°C	ASTME831	5.2E-06 cm/cm/°C
specific heat	50°C	DSC	1130 J/kg/°C
specific heat	specific heat	200°C	DSC	1620 J/kg/°C
thermal conductivity		ASTME1530	0.37 W/m/K

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD:3.18mm	ASTM D955	0.0-0.20 %
Shrinkage rate	Shrinkage rate	TD:3.18mm	ASTM D955	1.5-1.7 %
Water absorption rate	24hr	ASTM D570	0.10 %
melt mass-flow rate	400°C/2.16kg	ASTM D1238	1.1 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	105
Shore hardness	ShoreD,1Sec	ASTM D2240	92

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top