Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK KT-820CF30 SOLVAY USA
KetaSpire® PEEK
Solvay、Solvie, Belgium
Filler: Carbon fiber rein、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/KT-820CF30 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -- | ASTM D4812 | 750 J/m |
| -- | ISO 180 | 44 kJ/m² |
| hardness | Test Condition | Test Method | SOLVAY USA/KT-820CF30 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 105 |
| Shore hardness | 邵氏D,1秒 | ASTM D2240 | 92 |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/KT-820CF30 |
|---|---|---|---|
| elongation | 断裂4 | ASTM D638 | 2.0 % |
| Tensile modulus | --4 | ASTM D638 | 19700 Mpa |
| -- | ISO 527-2/1A/1 | 22800 Mpa | |
| tensile strength | -- | ASTM D638 | 201 Mpa |
| Flexural modulus | -- | ISO 178 | 20500 Mpa |
| elongation | 断裂 | ISO 527-2/1A/5 | 2.0 % |
| bending strength | -- | ISO 178 | 311 Mpa |
| Poisson's ratio | 7.58 0.42 | ||
| bending strength | -- | ASTM D790 | 317 Mpa |
| shear strength | ASTM D732 | 95.1 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/5 | 217 Mpa |
| Flexural modulus | -- | ASTM D790 | 17500 Mpa |
| compressive strength | ASTM D695 | 173 Mpa |
| flammability | Test Condition | Test Method | SOLVAY USA/KT-820CF30 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | SOLVAY USA/KT-820CF30 |
|---|---|---|---|
| melt viscosity | 400°C,1000sec^-1 | ASTM D3835 | 920 Pa·s |
| physical property | Test Condition | Test Method | SOLVAY USA/KT-820CF30 |
|---|---|---|---|
| Shrinkage rate | TD:3.18mm | ASTM D955 | 1.5-1.7 % |
| melt mass-flow rate | 400°C/2.16kg | ASTM D1238 | 1.1 g/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| Shrinkage rate | MD:3.18mm | ASTM D955 | 0.0-0.20 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/KT-820CF30 |
|---|---|---|---|
| thermal conductivity | ASTME1530 | 0.37 W/m/K | |
| Linear coefficient of thermal expansion | MD：-50到50°C | ASTME831 | 5.2E-06 cm/cm/°C |
| specific heat | 50°C | DSC | 1130 J/kg/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 315 °C |
| specific heat | 200°C | DSC | 1620 J/kg/°C |
| melting temperature | ASTM D3418 | 340 °C | |
| Glass Transition Temperature | ASTM D3418 | 150 °C |