PA66 Zytel® FR50-NC010 DUPONT USA
351
- Unit Price:US$ 5,914 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:110MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:PA66 Zytel® FR50-NC010 DUPONT CANADA
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:Fitness equipment｜Automotive sector｜Electrical field｜Electronic field｜Electrical appliances
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 阻燃 | ||
| purpose | 连接器 电器部件 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 240 °C |
| melting temperature | ISO 11357-3 | 262 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² | |
| 23°C | ISO 179/1eU | 60 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.6 | |
| shrinkage rate | 横向流量 | ISO 294-4 | 0.80 % |
| 流量 | ISO 294-4 | 0.30 % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 62631-3-2 | -- ohms | |
| volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| dielectric strength | 2.00 mm | IEC 60243-1 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| mold temperature | 70 to 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| pressure holding | 50.0 to 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638/ISO 527 | 10600 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 9450 kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ISO 527-2 | 10200 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 170 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.