PA66 FR50-NC010 DUPONT USA
Zytel®
Fitness equipment,Automotive sector,Electrical field,Electronic field,Electrical appliances
Flame retardant,Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 50 kJ/m² |
| 23°C | ISO 179/1eU | 60 kJ/m² | |
| -30°C | ISO 179/1eU | 50 kJ/m² |
| thermal performance | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 240 °C |
| melting temperature | ISO 11357-3 | 262 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| Tensile modulus | ASTM D638/ISO 527 | 10600 kg/cm²(MPa)[Lb/in²] | |
| ISO 527-2 | 10200 Mpa | ||
| tensile strength | 断裂 | ISO 527-2 | 170 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
| flexural modulus | ASTM D790/ISO 178 | 9450 kg·cm/cm(J/M)ft·lb/in |
| Electrical performance | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| dielectric strength | 2.00 mm | IEC 60243-1 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| Surface Resistivity | IEC 62631-3-2 | -- ohms |
| other | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| characteristic | 阻燃 | ||
| purpose | 连接器 电器部件 |
| Physical properties | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 0.80 % | |
| density | ASTM D792/ISO 1183 | 1.6 | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.60 % |
| flammability | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| injection | Test Condition | Test Method | DUPONT USA/FR50-NC010 |
|---|---|---|---|
| pressure holding | 50.0 to 100 Mpa | ||
| Maximum Screw Tangential Speed | 12 m/min | ||
| pressure holding | Drying Recommended | yes | |
| Suggested maximum moisture content | 0.20 % | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| mold temperature | 70 to 120 °C | ||
| drying temperature | 80 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Mold Temperature, Optimum | 100 °C |