PC TARFLON™ IRY2200 IDEMITSU JAPAN
291
- Unit Price:US$ 2,902 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:25MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent｜Flame retardant｜High temperature resistance｜Low viscosity
- Application Areas:currency
- Color:--
- Grade:Weather resistant grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | 85-89 % |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 标准、非臭素、阻燃 |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 0.5-0.7% % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 12 g/10min | ||
| Water absorption rate | 0.23 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 80 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | tB 90 % | |
| tensile strength | ASTM D638/ISO 527 | Y 65 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | R120.M50 | |
| Flexural modulus | ASTM D790/ISO 178 | 2.3(GPa) kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 90 KJ/m | ||
| elongation at break | 115 % | ||
| Flexural modulus | 2350 Mpa | ||
| tensile strength | 64 Mpa | ||
| sliding friction | 12 | ||
| Tensile strength | 68 Mpa | ||
| Tensile modulus | 2300 Mpa | ||
| bending strength | 93 Mpa | ||
| Rockwell hardness | R120（M75） | ||
| Impact strength of cantilever beam gap | 70 KJ/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 2.85 | |
| arc resistance | 110 sec | ||
| permittivity | 2.91 | ||
| Volume resistivity | ＜10 Ω.m | ||
| permittivity | 2.85 | ||
| dielectric loss tangent | 9.2×10 | ||
| 6.6×10 | |||
| dielectric strength | 30 KV/mm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.2 | |
| Shrinkage rate | ASTM D955 | 0.5-0.7 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 12 cm3/10min(300℃/1.2kg ) g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.23 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0/3.0mm | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 6.5 mm/mm.℃ | |
| combustibility | V-0 | ||
| Heat distortion temperature | 148 °C | ||
| vicat | 148 °C | ||
| Linear coefficient of thermal expansion | 6.5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.