Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC IRY2200 IDEMITSU JAPAN
TARFLON™
currency
transparent,Flame retardant,High temperature resistan,Low viscosity
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| Water absorption rate | 0.23 % | ||
| melt mass-flow rate | 12 g/10min |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| permittivity | 1MHz | 2.85 | |
| arc resistance | 110 sec | ||
| Volume resistivity | ＜10 Ω.m | ||
| dielectric loss tangent | 1MHz | 9.2×10 | |
| dielectric strength | 30 KV/mm | ||
| dielectric constant | ASTM D150/IEC 60250 | 2.85 | |
| dielectric loss tangent | 60Hz | 6.6×10 | |
| permittivity | 60Hz | 2.91 |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 80 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2.3(GPa) kg/cm²(MPa)[Lb/in²] | |
| bending strength | 93 Mpa | ||
| Rockwell hardness | R120（M75） | ||
| Impact strength of cantilever beam gap | 4mm | 70 KJ/m | |
| elongation at break | ASTM D638/ISO 527 | tB 90 % | |
| Rockwell hardness | ASTM D785 | R120.M50 | |
| tensile strength | ASTM D638/ISO 527 | Y 65 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 3.2mm | 90 KJ/m | |
| sliding friction | 12 | ||
| Tensile strength | 68 Mpa | ||
| Flexural modulus | 2350 Mpa | ||
| Tensile modulus | 2300 Mpa | ||
| tensile strength | 屈服 | 64 Mpa | |
| elongation at break | 115 % |
| other | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| characteristic | 标准、非臭素、阻燃 |
| Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5-0.7 % | |
| density | ASTM D792/ISO 1183 | 1.2 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 12 cm3/10min(300℃/1.2kg ) g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.23 % |
| processability | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| Shrinkage rate | 0.5-0.7% % |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| transmittance | 85-89 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/IRY2200 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0/3.0mm | |
| vicat | 148 °C | ||
| Heat distortion temperature | 148 °C | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 6.5 mm/mm.℃ | |
| combustibility | 3mm | V-0 | |
| Linear coefficient of thermal expansion | 6.5 |