PC PANLITE® ML-3206ZT TEIJIN JAPAN
298
- Unit Price:US$ 4,406 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent｜optical performance
- Application Areas:Casters
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | 1.5mmt | JIS K7136 | 85 % |
| Pigment dispersion | 2.0mmt | In-house method | 17 % |
| transmittance | ASTM D1003/ISO 13468 | 2MM 86% % |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.80MPa | ISO 75-1 | 129 °C |
| 线膨胀系数，MD | ISO 11359-2 | 0.7 X10-4/℃ | |
| TD | ISO 11359-2 | 0.7 X10-4/℃ | |
| UL flame retardant rating | 1.0mm | UL 94 | V-2 |
| Combustibility (rate) | UL 94 | V-2（相当） | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 134 ℃（℉） |
| HDT | ASTM D648/ISO 75 | 129 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 帝人高透光光扩散PC.阻燃V-2.抗UV | ||
| Color | 半透明. | ||
| purpose | LED球泡灯罩 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissolving fingers | 300℃ | ISO 1133 | 18 cm310min |
| shrinkage rate | MD | In-house method | 0.5-0.7 % |
| TD | In-house method | 0.5-0.7 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 50mm/min，屈服 | ISO 527-1 | 61 Mpa |
| 50mm/min，断裂 | ISO 527-1 | 68 Mpa | |
| Elongation at break | 50mm/min | ISO 527-1 | 105 % |
| flexural modulus | 2mm/min | ISO 178 | 2400 Mpa |
| bending strength | 2mm/min | ISO 178 | 99 Mpa |
| Impact strength of cantilever beam gap | Notched | ISO 179 | 10 kJ/m² |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 25 kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 25 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 120 % | |
| Tensile modulus | ASTM D638/ISO 527 | 66 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 61 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 96 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 120 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.