PC ML-3206ZT TEIJIN JAPAN
PANLITE®
Casters
transparent,optical performance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3206ZT |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 25 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 96 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | 50mm/min | ISO 527-1 | 105 % |
| tensile strength | 50mm/min，断裂 | ISO 527-1 | 68 Mpa |
| elongation at break | ASTM D638/ISO 527 | 120 % | |
| tensile strength | ASTM D638/ISO 527 | 61 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | Notched | ISO 179 | 10 kJ/m² |
| tensile strength | 50mm/min，屈服 | ISO 527-1 | 61 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 66 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 25 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | 2mm/min | ISO 178 | 99 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 2400 Mpa |
| optical performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3206ZT |
|---|---|---|---|
| Pigment dispersion | 2.0mmt | In-house method | 17 % |
| transmittance | 1.5mmt | JIS K7136 | 85 % |
| ASTM D1003/ISO 13468 | 2MM 86% % |
| other | Test Condition | Test Method | TEIJIN JAPAN/ML-3206ZT |
|---|---|---|---|
| characteristic | 帝人高透光光扩散PC.阻燃V-2.抗UV | ||
| Color | 半透明. | ||
| purpose | LED球泡灯罩 |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/ML-3206ZT |
|---|---|---|---|
| Dissolving fingers | 300℃ | ISO 1133 | 18 cm310min |
| Shrinkage rate | MD | In-house method | 0.5-0.7 % |
| TD | In-house method | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3206ZT |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-2（相当） | |
| Heat distortion temperature | TD，HDT | ISO 11359-2 | 0.7 X10-4/℃ |
| 线膨胀系数，MD，HDT | ISO 11359-2 | 0.7 X10-4/℃ | |
| HDT | ASTM D648/ISO 75 | 129 ℃（℉） | |
| UL flame retardant rating | 1.0mm | UL 94 | V-2 |
| Heat distortion temperature | 1.80MPa，HDT | ISO 75-1 | 129 °C |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |