PP POLYFORT® RPP 2000 A SCHULMAN USA

288

Unit Price:US$ 1,543 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Halogen-free
Application Areas:--
Color:--
Grade:Halogen-free flame retardant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	17 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result
Burning rate	0.750mm,Self-Extinguishing	ISO 3795	0.0 mm/min
	Burning rate	1.50mm,自动灭火	ISO 3795	0.0 mm/min
	Burning rate	Burning rate	3.00mm,自动灭火	ISO 3795	0.0 mm/min
UL flame retardant rating	0.75mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-2
		UL flame retardant rating	3.0mm	UL 94	V-2
			UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	V-2
				UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-2
				UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	V-2
Burning wire flammability index	0.75mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	725 °C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	725 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725 °C
Extreme Oxygen Index		ISO 4589-2	27 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	1800 Mpa
tensile strength	Yield	ISO 527-2/1A/50	38.0 Mpa
Tensile strain	Yield	ISO 527-2/1A/50	8.0 %

thermal performance	Test Condition	Test Method	Test Result
RTI Elec	1.5mm	UL 746	65.0 °C
RTI Elec	RTI Elec	3.0mm	UL 746	65.0 °C
RTI Imp	0.75mm	UL 746	65.0 °C
	RTI Imp	1.5mm	UL 746	65.0 °C
	RTI Imp	RTI Imp	3.0mm	UL 746	65.0 °C
RTI Str	0.75mm	UL 746	65.0 °C
	RTI Str	1.5mm	UL 746	65.0 °C
	RTI Str	RTI Str	3.0mm	UL 746	65.0 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	102 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	59.0 °C
Vicat softening temperature	--	ISO 306/A50	157 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	97.0 °C
Ball Pressure Test	145°C	IEC 60695-10-2	Pass
RTI Elec	0.75mm	UL 746	65.0 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	8.00 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PP POLYFORT® RPP 2000 A SCHULMAN USA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet