Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP RPP 2000 A SCHULMAN USA
POLYFORT®
--
Halogen-free
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/RPP 2000 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| -30°C | ISO 179/1eU | 17 kJ/m² |
| Electrical performance | Test Condition | Test Method | A SCHULMAN USA/RPP 2000 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/RPP 2000 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 8.0 % |
| Tensile modulus | ISO 527-2/1A/1 | 1800 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 38.0 Mpa |
| flammability | Test Condition | Test Method | A SCHULMAN USA/RPP 2000 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | V-2 |
| 0.75mm | UL 94 | V-2 | |
| 0.75mm | IEC 60695-11-10,-20 | V-2 | |
| 3.0mm | UL 94 | V-2 | |
| 1.5mm | IEC 60695-11-10,-20 | V-2 | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 725 °C |
| burning rate | 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| burning rate | 0.750mm,Self-Extinguishing | ISO 3795 | 0.0 mm/min |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| burning rate | 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 725 °C |
| physical property | Test Condition | Test Method | A SCHULMAN USA/RPP 2000 |
|---|---|---|---|
| Melt volume flow rate | 230°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/RPP 2000 |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 65.0 °C |
| RTI Imp | 1.5mm | UL 746 | 65.0 °C |
| RTI Elec | 3.0mm | UL 746 | 65.0 °C |
| RTI Imp | 3.0mm | UL 746 | 65.0 °C |
| RTI Elec | 0.75mm | UL 746 | 65.0 °C |
| RTI Imp | 0.75mm | UL 746 | 65.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 59.0 °C |
| vicat | -- | ISO 306/A50 | 157 °C |
| RTI Str | 1.5mm | UL 746 | 65.0 °C |
| vicat | -- | ISO 306/B50 | 97.0 °C |
| RTI Str | 3.0mm | UL 746 | 65.0 °C |
| RTI Elec | 1.5mm | UL 746 | 65.0 °C |
| ball-indentation hardness | 145°C | IEC 60695-10-2 | Pass |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 102 °C |