PA66

PA66 Leona™  MR001 ASAHI JAPAN

225
  • Unit Price:US$ 3,600 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    43.6MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:high strength｜High rigidity
  • Application Areas:Automotive Applications｜Gears
  • Color:--
  • Grade:Enhanced level

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 17962 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.75mmUL 94HB
Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate湿1.5 %
mechanical propertiesTest ConditionTest MethodTest Result
Taber abraser1000CyclesASTM D1044-- mg
Tensile modulus23°CISO 527-25900 Mpa
tensile strengthYield,23°CISO 527-2-- Mpa
tensile strengthASTM D63898.0 Mpa
bending strength23°CISO 178150 Mpa
Rockwell hardnessASTM D785R120
Elongation at Break干(湿)ASTM D-6386(7) %
flexural coefficient干(湿)ASTM D-7905.6(3.3) GPa
Rockwell hardness干(湿)ASTM D-785120(108) R scale
bending strength干(湿)ASTM D-790157(98) Mpa
Impact strength of cantilever beam gap干(湿)ASTM D-25634(39) J/m
Rockwell hardness干(湿)ASTM D-78585(60) M Scale
tensile strength干(湿)ASTM D-63898(67) Mpa
tensile strengthBreak,23°CISO 527-293.0 Mpa
Tensile strainYield,23°CISO 527-2-- %
elongationBreakASTM D6386.0 %
Tensile strainBreak,23°CISO 527-25.5 %
Bending modulusASTM D7905600 Mpa
Bending modulus23°CISO 1785800 Mpa
bending strengthASTM D790157 Mpa
Bending modulusASTM D790/ISO 1785590(MPa) kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 178157(MPa) kg·cm/cm(J/M)ft·lb/in
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionMDASTM D6966E-05 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A118 °C
Hot deformation temperature1.8MPa,UnannealedASTM D648160 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B229 °C
Hot deformation temperature0.45MPa,UnannealedASTM D648240 °C
Linear coefficient of thermal expansion干ASTM D-6966
Hot deformation temperature0.46MPa,干ASTM D-648240 °C
UL flame retardant rating干UL 94HB
Hot deformation temperature1.82MPa,干ASTM D-648160 °C
Linear coefficient of thermal expansionASTM D696/ISO 113596 mm/mm.℃
Combustibility (rate)UL 94HB
Hot deformation temperatureHDTASTM D648/ISO 75240 ℃（℉）
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 62-- %
Water absorption rateSaturation,23°C-- %
Shrinkage rateMDInternal Method1.0-1.1 %
Wear factor湿ASTM D-104422
Shrinkage rate干旭化成方法1.0-1.1 %
densityASTM D792/ISO 11831.52
Shrinkage rateASTM D9551.0-1.1 %
Water absorption rateASTM D570/ISO 621.5 %
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strengthASTM D14922 KV/mm
Volume resistivity23°CIEC 600931E+14 ohms·cm
Volume resistivityASTM D2571E+14 ohms·cm
Surface resistivityIEC 600931E+13 ohms
Surface resistivityASTM D2571E+13 ohms
Dielectric strengthIEC 60243-122 KV/mm
Arc resistanceASTM D495/IEC 6011287
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-SaleISO 2039-2120
Rockwell hardnessM-SaleISO 2039-285
Rockwell hardnessR-SaleASTM D785120
Rockwell hardnessM-SaleASTM D78585
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.