PA66 MR001 ASAHI JAPAN
Leona™
Automotive Applications,Gears
high strength,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 62 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 85 |
| R计秤 | ISO 2039-2 | 120 | |
| M计秤 | ISO 2039-2 | 85 | |
| R计秤 | ASTM D785 | 120 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Water absorption rate | 湿 | 1.5 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 34(39) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 5.6(3.3) GPa |
| bending strength | ASTM D790 | 157 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 5900 Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 98(67) Mpa |
| 断裂,23°C | ISO 527-2 | 93.0 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 5590(MPa) kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 157(MPa) kg·cm/cm(J/M)ft·lb/in | |
| Rockwell hardness | ASTM D785 | R120 | |
| Flexural modulus | ASTM D790 | 5600 Mpa | |
| tensile strength | ASTM D638 | 98.0 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(108) R scale |
| 干(湿) | ASTM D-785 | 85(60) M Scale | |
| elongation | 断裂 | ASTM D638 | 6.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 5.5 % |
| bending strength | 23°C | ISO 178 | 150 Mpa |
| 干(湿) | ASTM D-790 | 157(98) Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | -- Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | -- % |
| Flexural modulus | 23°C | ISO 178 | 5800 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 6(7) % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 22 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+13 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | ASTM D149 | 22 KV/mm | |
| arc resistance | ASTM D495/IEC 60112 | 87 | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.0-1.1 % | |
| density | ASTM D792/ISO 1183 | 1.52 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.5 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.0-1.1 % |
| Water absorption rate | 饱和,23°C | -- % | |
| 平衡,23°C,50%RH | ISO 62 | -- % | |
| Wear factor | 湿 | ASTM D-1044 | 22 |
| Shrinkage rate | 干 | 旭化成方法 | 1.0-1.1 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/MR001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 160 °C |
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 240 °C |
| 1.82MPa,干，HDT | ASTM D-648 | 160 °C | |
| HDT | ASTM D648/ISO 75 | 240 ℃（℉） | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 229 °C | |
| 0.46MPa,干，HDT | ASTM D-648 | 240 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 118 °C | |
| UL flame retardant rating | 干 | UL 94 | HB |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 6E-05 cm/cm/°C |
| 干 | ASTM D-696 | 6 | |
| ASTM D696/ISO 11359 | 6 mm/mm.℃ |