PBT DURANEX® 3405 JAPAN POLYPLASTIC
180
- Unit Price:US$ 2,785 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Electronic and electrical components｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 100 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 214 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 1E-05 cm/cm/°C |
| TD：23to55°C | 内部方法 | 7E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8Mpa | ASTM D75-1 | 214 °C |
| UL flame retardant rating | UL 94 | HB | |
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | - mm/mm.℃ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| density | ASTM D792/ISO 1183 | 1.7 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 24 KV/mm |
| volume resistivity | IEC 60093 | 3×1016 Ω.cm | |
| Surface Resistivity | IEC 60093 | 4×1016 Ω | |
| volume resistivity | ASTM D257/IEC 60093 | 3.0 x 10^16 Ω.cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 162 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.7 % |
| flexural modulus | ISO 178 | 14500 Mpa | |
| bending strength | ISO 178 | 254 Mpa | |
| tensile strength | ASTM D527-1 | 162 Mpa | |
| Tensile strain | 断裂 | ASTM D527-1 | 1.7 % |
| bending strength | ASTM D178 | 254 Mpa | |
| flexural modulus | ASTM D178 | 14500 Mpa | |
| Charpy Notched Impact Strength | ASTM D179/1eA | 16.0 kJ/m² | |
| tensile strength | ASTM D638/ISO 527 | 162 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 14500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 254 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 1.7 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.