Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 3405 JAPAN POLYPLASTIC
DURANEX®
Electronic and electrical components,Automotive Applications
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 100 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 254 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D179/1eA | 16.0 kJ/m² | |
| Flexural modulus | ASTM D790/ISO 178 | 14500 kg/cm²(MPa)[Lb/in²] | |
| ASTM D178 | 14500 Mpa | ||
| elongation at break | ASTM D638/ISO 527 | 1.7 % | |
| tensile strength | ASTM D638/ISO 527 | 162 kg/cm²(MPa)[Lb/in²] | |
| ISO 527-2 | 162 Mpa | ||
| Tensile strain | 断裂 | ASTM D527-1 | 1.7 % |
| bending strength | ASTM D178 | 254 Mpa | |
| ISO 178 | 254 Mpa | ||
| Tensile strain | 断裂 | ISO 527-2 | 1.7 % |
| Flexural modulus | ISO 178 | 14500 Mpa | |
| tensile strength | ASTM D527-1 | 162 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 24 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 3.0 x 10^16 Ω.cm | |
| IEC 60093 | 3×1016 Ω.cm | ||
| Surface Resistivity | IEC 60093 | 4×1016 Ω |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.7 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/3405 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 7E-05 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 214 °C |
| 1.8Mpa，HDT | ASTM D75-1 | 214 °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | - mm/mm.℃ | |
| UL flame retardant rating | UL 94 | HB |