Material Properties:High mobility｜High ductility at low temperature｜High modulus
Application Areas:Thin walled products｜Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 6.40 mm	ASTM D648	97.0 °C
	Heat Deflection Temperature	1.8 MPa, 未退火, 3.20 mm	ASTM D648	83.0 °C
		Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm	ASTM D648	89.0 °C
		Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10	ISO 75-2/Af	80.0 °C
vicat	--	ASTM D152511	91.0 °C
	vicat	--	ISO 306/B50	98.0 °C
	vicat	vicat	--	ISO 306/B120	102 °C
ball-indentation hardness	73 到 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	流动 : -40 到 40°C	ASTM E831	5.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	横向 : -40 到 40°C	ASTM E831	6.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : -40°C	ISO 11359-2	6.0E-5 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.60 mm	UL 94	V-1
	UL flame retardant rating	0.8 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	5VB
Burning wire flammability index	0.8 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	50.0 J

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	18 g/10 min
Melt volume flow rate	220°C/5.0 kg	ISO 1133	14.0 cm3/10min
shrinkage rate	流动 : 3.20 mm	内部方法	0.30 - 0.50 %
shrinkage rate	shrinkage rate	横向流动 : 3.20 mm	内部方法	0.40 - 0.60 %
Water absorption rate	24 hr	ASTM D570	0.10 %
	Water absorption rate	24 hr, 50% RH	ASTM D570	0.010 %
		Water absorption rate	饱和, 23°C	ISO 62	0.090 %
		Water absorption rate	Water absorption rate	平衡, 23°C, 50% RH	ISO 62	0.010 %

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		ASTM D257	3.5E+15 ohms
volume resistivity		ASTM D257	2.7E+16 ohms·cm

injection	Test Condition	Test Method	Test Result
drying temperature			90 °C
drying time			> 4.0 hr
Suggested maximum moisture content			0.040 %
Temperature at the rear of the barrel			275 to 300 °C
Temperature in the middle of the barrel			275 to 300 °C
Temperature at the front of the material cylinder			280 to 300 °C
Spray nozzle temperature			280 to 300 °C
Processing (melt) temperature			275 to 300 °C
mold temperature			60 to 80 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	3500 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	3200 Mpa
tensile strength	屈服3	ASTM D638	65.0 Mpa
	tensile strength	屈服4	ASTM D638	65.0 Mpa
		tensile strength	断裂4	ASTM D638	50.0 Mpa
		tensile strength	tensile strength	断裂	ISO 527-2/5	50.0 Mpa
elongation	屈服4	ASTM D638	4.0 %
	elongation	屈服	ISO 527-2/5	3.5 %
		elongation	断裂4	ASTM D638	100 %
		elongation	elongation	断裂	ISO 527-2/50	15 %
flexural modulus	50.0 mm 跨距5	ASTM D790	3300 Mpa
flexural modulus	flexural modulus	--6	ISO 178	3450 Mpa
bending strength	--6,7	ISO 178	97.0 Mpa
bending strength	bending strength	屈服, 50.0 mm 跨距5	ASTM D790	100 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.