Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CM6140 WH SABIC INNOVATIVE NANSHA
CYCOLOY™
Thin walled products,Electronic and electrical components
High mobility,High ductility at low tem,High modulus
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6140 WH |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 5.0 kJ/m² | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 50.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6140 WH |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 3500 Mpa |
| tensile strength | 屈服4 | ASTM D638 | 65.0 Mpa |
| 断裂 | ISO 527-2/5 | 50.0 Mpa | |
| elongation | 断裂4 | ASTM D638 | 100 % |
| tensile strength | 屈服3 | ASTM D638 | 65.0 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 3300 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 15 % |
| bending strength | --6,7 | ISO 178 | 97.0 Mpa |
| Flexural modulus | --6 | ISO 178 | 3450 Mpa |
| bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 100 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 3.5 % |
| 屈服4 | ASTM D638 | 4.0 % | |
| tensile strength | 断裂4 | ASTM D638 | 50.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 3200 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6140 WH |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 2.7E+16 ohms·cm | |
| Surface Resistivity | ASTM D257 | 3.5E+15 ohms |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6140 WH |
|---|---|---|---|
| UL flame retardant rating | 0.60 mm | UL 94 | V-1 |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 800 °C |
| Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6140 WH |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.010 % |
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.60 % |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.010 % |
| 24 hr | ASTM D570 | 0.10 % | |
| melt mass-flow rate | 260°C/2.16 kg | ASTM D1238 | 18 g/10 min |
| Melt volume flow rate | 220°C/5.0 kg | ISO 1133 | 14.0 cm3/10min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.30 - 0.50 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.090 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6140 WH |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 5.5E-5 cm/cm/°C |
| vicat | -- | ASTM D152511 | 91.0 °C |
| -- | ISO 306/B120 | 102 °C | |
| ball-indentation hardness | 73 到 77°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 6.0E-5 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 98.0 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 89.0 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 6.0E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 97.0 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 83.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10，HDT | ISO 75-2/Af | 80.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CM6140 WH |
|---|---|---|---|
| drying time | > 4.0 hr | ||
| Suggested maximum moisture content | 0.040 % | ||
| Temperature in the middle of the barrel | 275 to 300 °C | ||
| Temperature at the rear of the barrel | 275 to 300 °C | ||
| Processing (melt) temperature | 275 to 300 °C | ||
| drying temperature | 90 °C | ||
| Temperature at the front of the material cylinder | 280 to 300 °C | ||
| Temperature | 60 to 80 °C | ||
| Spray nozzle temperature | 280 to 300 °C |