Material Description

Material Properties:Glass fiber reinforced｜Flame retardant｜enhance
Application Areas:Automotive sector｜Electrical field｜Electronic field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	3.0 mm	UL 94	5VA
	UL flame retardant rating	UL flame retardant rating	0.40 mm	UL 94	V-2
Extreme Oxygen Index		ISO 4589-2	47 %
Burning wire flammability index	3.2 mm	IEC 60695-2-12	960 °C

mechanical properties	Test Condition	Test Method	Test Result
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	10.0 mg
bending strength		ISO 178	160 Mpa
Bending modulus		ISO 178	3300 Mpa
Tensile strain	Break	ISO 527-2/50	60 %
Tensile strain	Tensile strain	Yield	ISO 527-2/50	6.0 %
tensile strength	Break	ISO 527-2/50	85.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	105 Mpa
Tensile modulus		ISO 527-2/1	3200 Mpa

injection	Test Condition	Test Method	Test Result
Temperature at the rear of the barrel			340 to 395 °C
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Hopper temperature			80 to 120 °C
Temperature in the middle of the barrel			350 to 405 °C
Temperature at the front of the material cylinder			360 to 415 °C
Spray nozzle temperature			350 to 405 °C
Processing (melt) temperature			370 to 410 °C
Mold temperature			140 to 180 °C

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow : 23 to 150°C	ISO 11359-2	5.0E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.24 W/m/K
RTI Elec		UL 746	170 °C
Linear coefficient of thermal expansion	Flow : 23 to 150°C	ISO 11359-2	5.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/A50	215 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	190 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	200 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ISO 306/B120	212 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	211 °C
RTI Imp		UL 746	170 °C
RTI		UL 746	170 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	1.3 %
Shrinkage rate	Flow	Internal Method	0.50 - 0.70 %
Melt Volume Flow Rate (MVR)	360°C/5.0 kg	ISO 1133	13.0 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	33 KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	25 KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	16 KV/mm
Relative permittivity	50 Hz	IEC 60250	2.90
Relative permittivity	Relative permittivity	60 Hz	IEC 60250	2.90
Compared to the anti leakage trace index	Solution B	IEC 60112	V
Relative permittivity	1 MHz	IEC 60250	2.90
Dissipation factor	50 Hz	IEC 60250	5.0E-4
	Dissipation factor	60 Hz	IEC 60250	5.0E-4
		Dissipation factor	1 MHz	IEC 60250	6.0E-3
		Dissipation factor	Dissipation factor	2.45 GHz	IEC 60250	2.5E-3
Compared to the anti leakage trace index	--	IEC 60112	V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H 358/30	ISO 2039-1	140 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.