PBT VALOX™  ENH4560 BK1066 SABIC INNOVATIVE SHANGHAI

197
  • Unit Price:US$ 6,198 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    35MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant｜Bromine free｜Chlorine free
  • Application Areas:Plastic bag｜Automotive External Parts
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

Filling analysisTest ConditionTest MethodTest Result
Melt viscosity260°C,1500sec^-1ISO 11443110 Pa·s
impact performanceTest ConditionTest MethodTest Result
23°CISO 180/1A9.0 kJ/m²
-30°CASTM D4812500 J/m
23°CASTM D4812500 J/m
-30°CISO 180/1U37 kJ/m²
23°CISO 180/1U37 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/2U35 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/2U40 kJ/m²
-30°CASTM D25675 J/m
0°CASTM D25675 J/m
23°CASTM D25675 J/m
-30°CISO 180/1A9.0 kJ/m²
0°CISO 180/1A9.0 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Hot filament ignition temperature1.00mmIEC 60695-2-13750 °C
Burning wire flammability index2.00mmIEC 60695-2-12960 °C
UL flame retardant rating3.00mmUL 945VB
UL flame retardant rating0.800mmUL 94V-0
Hot filament ignition temperature2.00mmIEC 60695-2-13750 °C
Hot filament ignition temperature3.00mmIEC 60695-2-13800 °C
mechanical propertiesTest ConditionTest MethodTest Result
crackASTM D638110 Mpa
yieldISO 527-2/5105 Mpa
yieldASTM D638110 Mpa
--1ASTM D63811000 Mpa
Fracture bending strainISO 1782.0 %
crackISO 527-2/5105 Mpa
yieldASTM D6382.0 %
yieldISO 527-2/52.0 %
crackASTM D6382.0 %
crackISO 527-2/52.0 %
50.0mm spanASTM D7909000 Mpa
--7ISO 17810000 Mpa
--8ISO 178170 Mpa
Yield, 50.0mm spanASTM D790150 Mpa
Fracture, 50.0mm spanASTM D790150 Mpa
thermal performanceTest ConditionTest MethodTest Result
RTIUL 746140 °C
RTI ImpUL 746125 °C
0.45MPa, unannealed, 3.20mmASTM D648223 °C
0.45MPa, unannealed, 64.0mm spanISO 75-2/Bf225224 °C
1.8MPa, unannealed, 3.20mmASTM D648210 °C
1.8MPa, unannealed, 64.0mm span ofISO 75-2/Af210 °C
Linear coefficient of thermal expansionMD:-40to40°CISO 11359-22E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD:23to150°CISO 11359-22.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:-40to40°CISO 11359-26.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:23to150°CISO 11359-21.5E-04 cm/cm/°C
RTI ElecUL 746140 °C
Physical propertiesTest ConditionTest MethodTest Result
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113316.0 cm3/10min
melt mass-flow rate265°C/5.0kgASTM D123823 g/10min
Electrical performanceTest ConditionTest MethodTest Result
3.20mm, inoilASTM D14918 KV/mm
1.60mm,inOilASTM D14922 KV/mm
0.800mm,inOilASTM D14932 KV/mm
Volume resistivityASTMD2571E+14 ohms·cm
Surface resistivityIEC 60093>1.0E+15 ohms
Hot wire ignitionHWIUL 746PLC 0
High arc combustion indexHAIUL 746PLC 0
Compared to the anti leakage trace indexIEC 60112PLC 0
Compared to the anti leakage trace indexCTIUL 746PLC 0
Dissipation factor1MHzASTMD1500.14
Dielectric constant1MHzASTMD1503.80
0.800mm, in oilIEC 60243-132 KV/mm
1.60mm, in oilIEC 60243-122 KV/mm
3.20mm, in oilIEC 60243-118 KV/mm
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestH358/30ISO 2039-1142 Mpa
Rockwell hardnessR-SaleISO 2039-2120
Supplementary InformationTest ConditionTest MethodTest Result
Filling materialASTM D22930 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.