PBT ENH4560 BK1066 SABIC INNOVATIVE SHANGHAI

VALOX™

Plastic bag,Automotive External Parts

Flame retardant,Bromine free,Chlorine free

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
Ball Pressure Test	H358/30	ISO 2039-1	142 Mpa
Rockwell hardness	R-Sale	ISO 2039-2	120

Supplementary Information	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
Filling material		ASTM D229	30 %

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
0.45MPa, unannealed, 3.20mm		ASTM D648	223 °C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	225224 °C
1.8MPa, unannealed, 3.20mm		ASTM D648	210 °C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	210 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	TD:-40to40°C	ISO 11359-2	6.2E-05 cm/cm/°C
		MD:23to150°C	ISO 11359-2	2.5E-05 cm/cm/°C
		TD:23to150°C	ISO 11359-2	1.5E-04 cm/cm/°C
		MD:-40to40°C	ISO 11359-2	2E-05 cm/cm/°C
RTI		UL 746	140 °C
RTI Elec		UL 746	140 °C
RTI Imp		UL 746	125 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
--1		ASTM D638	11000 Mpa
50.0mm span		ASTM D790	9000 Mpa
--7		ISO 178	10000 Mpa
--8		ISO 178	170 Mpa
crack		ASTM D638	110 Mpa
			ISO 527-2/5	105 Mpa
			ASTM D638	2.0 %
			ISO 527-2/5	2.0 %
Fracture, 50.0mm span		ASTM D790	150 Mpa
Fracture bending strain		ISO 178	2.0 %
yield		ASTM D638	2.0 %
			ISO 527-2/5	2.0 %
			ASTM D638	110 Mpa
			ISO 527-2/5	105 Mpa
Yield, 50.0mm span		ASTM D790	150 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
0.800mm,inOil		ASTM D149	32 KV/mm
0.800mm, in oil		IEC 60243-1	32 KV/mm
1.60mm,inOil		ASTM D149	22 KV/mm
1.60mm, in oil		IEC 60243-1	22 KV/mm
3.20mm, inoil		ASTM D149	18 KV/mm
3.20mm, in oil		IEC 60243-1	18 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0
Compared to the anti leakage trace index		CTI	UL 746	PLC 0
Dielectric constant	1MHz	ASTMD150	3.80
Dissipation factor	1MHz	ASTMD150	0.14
High arc combustion index	HAI	UL 746	PLC 0
Hot wire ignition	HWI	UL 746	PLC 0
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		ASTMD257	1E+14 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
melt mass-flow rate	265°C/5.0kg	ASTM D1238	23 g/10min
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	16.0 cm3/10min

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
0°C		ISO 180/1A	9.0 kJ/m²
0°C			ASTM D256	75 J/m
23°C		ASTM D256	75 J/m
			ASTM D4812	500 J/m
			ISO 180/1U	37 kJ/m²
			ISO 180/1A	9.0 kJ/m²
-30°C		ASTM D4812	500 J/m
			ASTM D256	75 J/m
			ISO 180/1A	9.0 kJ/m²
			ISO 180/1U	37 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/2U	40 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/2U	35 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
Burning wire flammability index	2.00mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	2.00mm	IEC 60695-2-13	750 °C
		3.00mm	IEC 60695-2-13	800 °C
		1.00mm	IEC 60695-2-13	750 °C
UL flame retardant rating	3.00mm	UL 94	5VB
UL flame retardant rating		0.800mm	UL 94	V-0

Filling analysis	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/ENH4560 BK1066
Melt viscosity	260°C,1500sec^-1	ISO 11443	110 Pa·s