PC PANLITE® ML-5206ZLP TEIJIN JAPAN

320

Unit Price:US$ 5,140 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
46MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜transparent
Application Areas:Casters｜Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	3000μm	ASTM D1003	77.0	%
Transmittance rate	1.5mmt	JIS K7136	85	%
Pigment dispersion	2.0mmt	In-house method	17	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875	°C
UL flame retardant rating	1.5mm	UL 94	V-0
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	875	°C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	2mm/min	ISO 178	98	Mpa
bending strength	bending strength		ISO 178	98.0	Mpa
Bending modulus		ISO 178	2400	Mpa
Nominal tensile fracture strain		ISO 527-2/50	25	%
Tensile strain	Yield	ISO 527-2/50	6.0	%
tensile strength	Break	ISO 527-2/50	53.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	65.0	Mpa
Tensile modulus		ISO 527-2/1	2400	Mpa
Impact strength of cantilever beam gap	Notched	ISO 179	8.0	kJ/m²
tensile strength	50mm/min，Yield	ISO 527-1	65	Mpa
tensile strength	tensile strength	50mm/min，Break	ISO 527-1	53	Mpa
Elongation at Break	50mm/min	ISO 527-1	25	%
Bending modulus	2mm/min	ISO 178	2400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec	1.5mm	UL 746	130	°C
RTI Imp	1.5mm	UL 746	125	°C
RTI	1.5mm	UL 746	130	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	122	°C
	Hot deformation temperature	1.80MPa	ISO 75-1	122	°C
		Hot deformation temperature	线膨胀系数，MD	ISO 11359-2	0.7	X10-4/℃
		Hot deformation temperature	Hot deformation temperature	TD	ISO 11359-2	0.7	X10-4/℃
UL flame retardant rating	1.5mm	UL 94	V-0
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.20	%
Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70	%
Shrinkage rate	Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	3.50	cm3/10min
Dissolving fingers	300℃	ISO 1133	3.5	cm310min
Shrinkage rate	MD	In-house method	0.5-0.7	%
Shrinkage rate	Shrinkage rate	TD	In-house method	0.5-0.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 2
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC PANLITE® ML-5206ZLP TEIJIN JAPAN

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index