PC ML-5206ZLP PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC TEIJIN JAPAN ML-5206ZLP

Injection grade

US$ 5,140 / MT

FOB Shenzhen Port

mechanical properties	Test Condition	Test Method	TEIJIN JAPAN/ML-5206ZLP
bending strength		ISO 178	98.0 Mpa
Bending modulus	2mm/min	ISO 178	2400 Mpa
tensile strength	50mm/min，Break	ISO 527-1	53 Mpa
bending strength	2mm/min	ISO 178	98 Mpa
Tensile modulus		ISO 527-2/1	2400 Mpa
Nominal tensile fracture strain		ISO 527-2/50	25 %
tensile strength	Break	ISO 527-2/50	53.0 Mpa
tensile strength		Yield	ISO 527-2/50	65.0 Mpa
Impact strength of cantilever beam gap	Notched	ISO 179	8.0 kJ/m²
tensile strength	50mm/min，Yield	ISO 527-1	65 Mpa
Bending modulus		ISO 178	2400 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Elongation at Break	50mm/min	ISO 527-1	25 %
flammability	Test Condition	Test Method	TEIJIN JAPAN/ML-5206ZLP
Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875 °C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	1.5mm	UL 94	V-0
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	875 °C
thermal performance	Test Condition	Test Method	TEIJIN JAPAN/ML-5206ZLP
UL flame retardant rating	1.5mm	UL 94	V-0
Hot deformation temperature	TD	ISO 11359-2	0.7 X10-4/℃
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Hot deformation temperature	1.80MPa	ISO 75-1	122 °C
Hot deformation temperature		线膨胀系数，MD	ISO 11359-2	0.7 X10-4/℃
RTI Imp	1.5mm	UL 746	125 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	130 °C
RTI	1.5mm	UL 746	130 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	122 °C
Physical properties	Test Condition	Test Method	TEIJIN JAPAN/ML-5206ZLP
Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %
Water absorption rate	23°C,24hr	ISO 62	0.20 %
Shrinkage rate	MD	In-house method	0.5-0.7 %
Shrinkage rate		TD:4.00mm	Internal Method	0.50-0.70 %
Dissolving fingers	300℃	ISO 1133	3.5 cm310min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	3.50 cm3/10min
Shrinkage rate	TD	In-house method	0.5-0.7 %
optical performance	Test Condition	Test Method	TEIJIN JAPAN/ML-5206ZLP
Transmittance rate	1.5mmt	JIS K7136	85 %
transmissivity	3000μm	ASTM D1003	77.0 %
Pigment dispersion	2.0mmt	In-house method	17 %
Electrical performance	Test Condition	Test Method	TEIJIN JAPAN/ML-5206ZLP
Compared to the anti leakage trace index		IEC 60112	PLC 2
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Surface resistivity		IEC 60093	>1.0E+15 ohms
impact performance	Test Condition	Test Method	TEIJIN JAPAN/ML-5206ZLP
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂