Material Properties:Oil resistant｜dimensional stability ｜Medium hardness｜Filler: Glass mineral｜40% filler by weight
Application Areas:Automotive sector｜Phone case｜Industrial components｜Industrial applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.48 g/cm³
density	density		ISO 1183	1.48 g/cm³
Shrinkage rate			0.40 %
Water absorption rate		ASTM D570	5.7 %
	Water absorption rate		ISO 62	5.7 %
		Water absorption rate		ASTM D570	1.7 %
		Water absorption rate	Water absorption rate		ISO 62	1.7 %

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638	123 Mpa
tensile strength	tensile strength		ISO 527-2	123 Mpa
elongation		ASTM D638	2.6 %
Tensile strain		ISO 527-2	2.7 %
Flexural modulus		ISO 178	7500 Mpa
Tensile modulus		ISO 527-2	7960 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	4.1 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	40 J/m
	Impact strength of cantilever beam gap		ASTM D256	53 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	4.8 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	198 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	199 °C
melting temperature		ASTM D3418	220 °C
melting temperature	melting temperature		ISO 3146	220 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.