PA6 B3GM35 BASF GERMANY
Ultramid®
Automotive sector,Phone case,Industrial components,Industrial applications
Oil resistant,dimensional stability ,Medium hardness,Filler: Glass mineral,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B3GM35 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.1 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 40 J/m |
| 23°C | ASTM D256 | 53 J/m | |
| 23°C | ISO 180 | 4.8 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3GM35 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.7 % |
| Flexural modulus | 23°C | ISO 178 | 7500 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 7960 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 123 Mpa |
| 断裂,23°C | ASTM D638 | 123 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 2.6 % |
| physical property | Test Condition | Test Method | BASF GERMANY/B3GM35 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.40 % | |
| Water absorption rate | 饱和 | ASTM D570 | 5.7 % |
| 平衡,50%RH | ASTM D570 | 1.7 % | |
| 平衡,23°C,50%RH | ISO 62 | 1.7 % | |
| 饱和,23°C | ISO 62 | 5.7 % | |
| density | ASTM D792 | 1.48 g/cm³ | |
| ISO 1183 | 1.48 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B3GM35 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 198 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 199 °C | |
| melting temperature | ASTM D3418 | 220 °C | |
| ISO 3146 | 220 °C |