Material Description
- Material Properties:Low warpage｜High mobility｜Flame retardant｜Glass fiber mineral reinforcement
- Application Areas:Fitness equipment｜Home appliance components｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 286 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 262 °C | |
| melting temperature | ISO 11357-3 | 328 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 9.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 3.8E-5 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 26 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+16 ohms | |
| volume resistivity | IEC 60093 | 1.0E+16 ohms·cm |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 150 to 170 °C | ||
| drying time | 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature at the rear of the barrel | 315 to 325 °C | ||
| Temperature in the middle of the barrel | 325 to 335 °C | ||
| Temperature at the front of the material cylinder | 330 to 350 °C | ||
| Spray nozzle temperature | 330 to 340 °C | ||
| Processing (melt) temperature | 335 to 345 °C | ||
| mold temperature | 80 to 130 °C | ||
| injection speed | 中等偏快 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 13000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 130 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.7 % |
| flexural modulus | 23°C | ISO 178 | 12700 Mpa |
| bending strength | 23°C | ISO 178 | 170 Mpa |
| Fracture bending strain | ISO 178 | 1.9 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.