LCP FIT30 CELANESE USA
VECTRA®
Fitness equipment、Home appliance components、Automotive Applications
Low warpage、High mobility、Flame retardant、Glass fiber mineral reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/FIT30 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 26 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/FIT30 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 170 Mpa |
| Flexural modulus | 23°C | ISO 178 | 12700 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 130 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.7 % |
| Fracture bending strain | ISO 178 | 1.9 % | |
| Tensile modulus | ISO 527-2/1A | 13000 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/FIT30 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1.0E+16 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1.0E+16 ohms |
| Thermal performance | Test Condition | Test Method | CELANESE USA/FIT30 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 328 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 286 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 262 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 9.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 3.8E-5 cm/cm/°C |
| injection | Test Condition | Test Method | CELANESE USA/FIT30 |
|---|---|---|---|
| drying time | 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature in the middle of the barrel | 325 to 335 °C | ||
| Temperature at the rear of the barrel | 315 to 325 °C | ||
| Processing (melt) temperature | 335 to 345 °C | ||
| drying temperature | 150 to 170 °C | ||
| Temperature at the front of the material cylinder | 330 to 350 °C | ||
| Temperature | 80 to 130 °C | ||
| injection speed | 中等偏快 | ||
| Spray nozzle temperature | 330 to 340 °C |