PPO NORYL™ SE1GFN1-780 SABIC INNOVATIVE JAPAN

Unit Price:US$ 3,639 /MT
Packaging Specification:
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Hydrolysis resistance
Application Areas:Automotive components｜Household appliances
Color:--
Grade:Injection grade

Technical Data Sheet

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	L -Sale	ASTM D785	104

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	131 °C
Vicat softening temperature		ASTM D15254	147 °C
RTI Elec		UL 746	110 °C
RTI Imp		UL 746	105 °C
RTI		UL 746	110 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	V-1
Extreme Oxygen Index		ASTM D2863	34 %

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	3.20 mm，Flow	Internal Method	0.30 - 0.50 %
Water absorption rate	24 hr	ASTM D570	0.070 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.22 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1.0E+15 ohms·cm
Dielectric constant	60 Hz	ASTM D150	3.00
	Dielectric constant	50 kHz	ASTM D150	3.00
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.00
Dissipation factor	50 Hz	ASTM D150	1.7E-3
	Dissipation factor	60 Hz	ASTM D150	1.7E-3
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	1.6E-3
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 2
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 1

injection	Test Condition	Test Method	Test Result
drying temperature			105 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			250 to 300 °C
Temperature in the middle of the barrel			260 to 305 °C
Temperature at the front of the material cylinder			270 to 310 °C
Spray nozzle temperature			280 to 310 °C
Processing (melt) temperature			280 to 310 °C
Mold temperature			75 to 105 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			20 to 100 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	74.0 Mpa
elongation	Break	ASTM D638	5.0 %
Bending modulus	50.0 mm Span	ASTM D790	3990 Mpa
bending strength	Break, 50.0 mm Span	ASTM D790	119 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ SE1GFN1-780 SABIC INNOVATIVE JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet