PC LEXAN™  EXL9335 SABIC INNOVATIVE US

161
  • Unit Price:US$ 5,368 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    44.5MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜Ductility at low temperature｜Short molding cycle
  • Application Areas:Electronic and Electrical Applications｜Aerospace Applications｜lens
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA50 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A50 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A75 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating2.5mmUL 945VA
Burning wire flammability index1.9mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13900 °C
UL flame retardant rating0.8mmUL 94V-0
UL flame retardant rating2.0mmUL 945VB
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulusISO 1782150 Mpa
Tensile modulusASTM D6382150 Mpa
Tensile modulusISO 527-2/12150 Mpa
bending strengthISO 17886.0 Mpa
tensile strengthYieldASTM D63859.0 Mpa
tensile strengthYieldISO 527-2/5059.0 Mpa
tensile strengthBreakASTM D63858.0 Mpa
tensile strengthBreakISO 527-2/5058.0 Mpa
elongationYieldASTM D6386.0 %
Tensile strainYieldISO 527-2/506.0 %
elongationBreakASTM D638100 %
Tensile strainBreakISO 527-2/50100 %
Bending modulus50.0mmSpanASTM D7902150 Mpa
Bending modulusISO 1782150 Mpa
Tensile modulusASTM D6382150 Mpa
Tensile modulusISO 527-2/12150 Mpa
bending strengthISO 17886.0 Mpa
bending strengthYield,50.0mmSpanASTM D79086.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
RTI ElecUL 746125 °C
RTI ImpUL 746110 °C
RTI StrUL 746125 °C
Vicat softening temperatureASTM D152511147 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
RTI ElecUL 746125 °C
RTI ImpUL 746110 °C
RTI StrUL 746125 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648139 °C
Hot deformation temperature0.45MPa,Unannealed,100mmSpanISO 75-2/Be139 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648126 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af126 °C
Vicat softening temperatureASTM D152511147 °C
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperature--ISO 306/B120147 °C
Physical propertiesTest ConditionTest MethodTest Result
densityASTM D7921.24 g/cm³
densityISO 11831.24 g/cm³
Outdoor applicabilityUL 746Cf1
melt mass-flow rate300°C/1.2kgASTM D12388.0 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11337.00 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.40-0.80 %
Shrinkage rateTD：3.20mmInternal Method0.40-0.80 %
Water absorption rateSaturation,23°CISO 620.12 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.050 %
Outdoor applicabilityUL 746Cf1
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace indexIEC 60112PLC 2
Compared to the anti leakage trace indexCTIUL 746PLC 2
Compared to the anti leakage trace indexIEC 60112PLC 2
High arc combustion indexHAIUL 746PLC 0
Hot wire ignitionHWIUL 746PLC 2
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.