Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9335 SABIC INNOVATIVE US
LEXAN™
Electronic and Electrical、Aerospace Applications、lens
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9335 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 50 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 50 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 75 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9335 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| tensile strength | 断裂 | ASTM D638 | 58.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 58.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2150 Mpa |
| Tensile modulus | ASTM D638 | 2150 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 59.0 Mpa |
| elongation | 断裂 | ASTM D638 | 100 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 86.0 Mpa |
| ISO 178 | 86.0 Mpa | ||
| Flexural modulus | ISO 178 | 2150 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 59.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9335 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9335 |
|---|---|---|---|
| Burning wire flammability index | 1.9mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| 2.0mm | UL 94 | 5VB | |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 900 °C |
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9335 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| Outdoor applicability | UL 746C | f1 | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 7.00 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.12 % | |
| density | ASTM D792 | 1.24 g/cm³ | |
| ISO 1183 | 1.24 g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EXL9335 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 139 °C |
| vicat | -- | ISO 306/B120 | 147 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 139 °C |
| vicat | -- | ISO 306/B50 | 145 °C |
| ASTM D152511 | 147 °C | ||
| RTI Imp | UL 746 | 110 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 126 °C |
| RTI Str | UL 746 | 125 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 126 °C |
| RTI Elec | UL 746 | 125 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |