thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8 MPa	ASTM D648	248 °C
Heat Deflection Temperature	Heat Deflection Temperature	0.45 MPa	ASTM D648	255 °C
Linear coefficient of thermal expansion	MD	ASTM D696	0.000030 1/℃

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	调节后	ASTM D256	63 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	干燥	ASTM D256	72 J/m

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0
Limiting Oxygen Index		ASTM D2863	37 %

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.52 g/cm³
shrinkage rate	TD	内部方法	0.9 %
shrinkage rate	shrinkage rate	MD	内部方法	0.4 %
Water absorption rate			0.9 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服	ASTM D638	123 Mpa
tensile strength	tensile strength	断裂	ASTM D638	153 Mpa
Tensile strain	调节后	ISO 527-2	2.5 %
Tensile strain	Tensile strain	干燥	ASTM D638	2.7 %
flexural modulus	调节后	ASTM D790	5900 Mpa
flexural modulus	flexural modulus	干燥	ASTM D790	7600 Mpa
bending strength	调节后	ASTM D790	177 Mpa
bending strength	bending strength	干燥	ASTM D790	216 Mpa
Taber abraser	1000 周期	ASTM D1044	24 mg
Rockwell hardness	M 级，调节后	ASTM D785	55
Rockwell hardness	Rockwell hardness	M 级，干燥	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.