Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 FG172X61 ASAHI JAPAN
Leona™
Electrical applications,switch,Hose
Glass fiber reinforced,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/FG172X61 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干燥 | ASTM D256 | 72 J/m |
| 调节后 | ASTM D256 | 63 J/m |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/FG172X61 |
|---|---|---|---|
| Tensile strain | 干燥 | ASTM D638 | 2.7 % |
| Taber abraser | 1000 周期 | ASTM D1044 | 24 mg |
| Tensile strain | 调节后 | ISO 527-2 | 2.5 % |
| tensile strength | 断裂 | ASTM D638 | 153 Mpa |
| Flexural modulus | 调节后 | ASTM D790 | 5900 Mpa |
| bending strength | 干燥 | ASTM D790 | 216 Mpa |
| tensile strength | 屈服 | ASTM D638 | 123 Mpa |
| Flexural modulus | 干燥 | ASTM D790 | 7600 Mpa |
| bending strength | 调节后 | ASTM D790 | 177 Mpa |
| Rockwell hardness | M 级，干燥 | ASTM D785 | 95 |
| M 级，调节后 | ASTM D785 | 55 |
| Flame retardant performance | Test Condition | Test Method | ASAHI JAPAN/FG172X61 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D2863 | 37 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/FG172X61 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.4 % |
| TD | 内部方法 | 0.9 % | |
| density | ISO 1183 | 1.52 g/cm³ | |
| Water absorption rate | 0.9 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/FG172X61 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa，HDT | ASTM D648 | 248 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 0.000030 1/℃ |
| Heat distortion temperature | 0.45 MPa，HDT | ASTM D648 | 255 °C |