PA66

PA66 Leona™  13G25 ASAHI JAPAN

225
  • Unit Price:US$ 3,337 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    87MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Creep resistance｜Fatigue resistance｜high strength｜High rigidity
  • Application Areas:Automotive sector｜Industrial applications｜Industrial machinery｜Electronic field｜Electrical field
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 17968 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.75mmUL 94HB
Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate湿1.9 %
mechanical propertiesTest ConditionTest MethodTest Result
Rockwell hardness干(湿)ASTM D-785120(-) R scale
Rockwell hardness干(湿)ASTM D-78596(74) M Scale
flexural coefficient干(湿)ASTM D-7908.1(4.7) GPa
Elongation at Break干(湿)ASTM D-6383(6) %
tensile strength干(湿)ASTM D-638180(110) Mpa
Impact strength of cantilever beam gap干(湿)ASTM D-256105(160) J/m
bending strength干(湿)ASTM D-790290(175) Mpa
bending strengthASTM D790290 Mpa
bending strength23°CISO 178275 Mpa
Taber abraser1000CyclesASTM D1044-- mg
Tensile modulus23°CISO 527-28200 Mpa
tensile strengthASTM D638180 Mpa
tensile strengthYield,23°CISO 527-2-- Mpa
tensile strengthBreak,23°CISO 527-2190 Mpa
Tensile strainYield,23°CISO 527-2-- %
elongationBreakASTM D6383.0 %
Tensile strainBreak,23°CISO 527-24.0 %
Bending modulusASTM D7908100 Mpa
Bending modulus23°CISO 1787800 Mpa
thermal performanceTest ConditionTest MethodTest Result
thermal conductivity0.30 W/m/K
Linear coefficient of thermal expansionMDASTM D6963E-05 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A245 °C
Hot deformation temperature1.8MPa,UnannealedASTM D648250 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B260 °C
Hot deformation temperature0.45MPa,UnannealedASTM D648260 °C
UL flame retardant rating干UL 94HB
Hot deformation temperature0.46MPa,干ASTM D-648260 °C
Linear coefficient of thermal expansion干ASTM D-6963 ×10-5/K
thermal conductivity干0.3 W/(m.K)
Hot deformation temperature1.82MPa,干ASTM D-648250 °C
Physical propertiesTest ConditionTest MethodTest Result
Wear factor湿ASTM D-104412 ×10-6kg/1000times
Shrinkage rate干旭化成方法0.5/0.9 %
Water absorption rateEquilibrium,23°C,50%RHISO 62-- %
Shrinkage rateTDInternal Method0.90 %
Shrinkage rateMDInternal Method0.50 %
Shrinkage rate吸水率(Saturation,23°C)Internal Method-- %
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace index3.00mmIEC 60112PLC 0
Dielectric strengthIEC 60243-129 KV/mm
Dielectric strengthASTM D14929 KV/mm
Surface resistivityASTM D2571E+15 ohms
Surface resistivityIEC 600931E+15 ohms
Volume resistivityASTM D2571E+15 ohms·cm
Volume resistivity23°CIEC 600931E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM-SaleASTM D78596
Rockwell hardnessR-SaleASTM D785120
Rockwell hardnessM-SaleISO 2039-296
Rockwell hardnessR-SaleISO 2039-2120
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.