PA66 13G25 ASAHI JAPAN

Leona™

Automotive sector,Industrial applications,Industrial machinery,Electronic field,Electrical field

Creep resistance,Fatigue resistance,high strength,High rigidity

Plastic Datasheets

hardness	Test Condition	Test Method	ASAHI JAPAN/13G25
Rockwell hardness	M-Sale	ASTM D785	96
		M-Sale	ISO 2039-2	96
		R-Sale	ISO 2039-2	120
		R-Sale	ASTM D785	120

Basic Performance	Test Condition	Test Method	ASAHI JAPAN/13G25
Water absorption rate	湿		1.9 %

thermal performance	Test Condition	Test Method	ASAHI JAPAN/13G25
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	250 °C
		0.45MPa,Unannealed	ISO 75-2/B	260 °C
		1.82MPa,干	ASTM D-648	250 °C
		1.8MPa,Unannealed	ISO 75-2/A	245 °C
		0.45MPa,Unannealed	ASTM D648	260 °C
		0.46MPa,干	ASTM D-648	260 °C
Linear coefficient of thermal expansion	干	ASTM D-696	3 ×10-5/K
Linear coefficient of thermal expansion		MD	ASTM D696	3E-05 cm/cm/°C
thermal conductivity	干		0.3 W/(m.K)
thermal conductivity				0.30 W/m/K
UL flame retardant rating	干	UL 94	HB

mechanical properties	Test Condition	Test Method	ASAHI JAPAN/13G25
Bending modulus		ASTM D790	8100 Mpa
Bending modulus		23°C	ISO 178	7800 Mpa
bending strength	干(湿)	ASTM D-790	290(175) Mpa
		23°C	ISO 178	275 Mpa
			ASTM D790	290 Mpa
elongation	Break	ASTM D638	3.0 %
Elongation at Break	干(湿)	ASTM D-638	3(6) %
flexural coefficient	干(湿)	ASTM D-790	8.1(4.7) GPa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	105(160) J/m
Rockwell hardness	干(湿)	ASTM D-785	96(74) M Scale
Rockwell hardness		干(湿)	ASTM D-785	120(-) R scale
Taber abraser	1000Cycles	ASTM D1044	-- mg
Tensile modulus	23°C	ISO 527-2	8200 Mpa
Tensile strain	Yield,23°C	ISO 527-2	-- %
Tensile strain		Break,23°C	ISO 527-2	4.0 %
tensile strength	Break,23°C	ISO 527-2	190 Mpa
		干(湿)	ASTM D-638	180(110) Mpa
			ASTM D638	180 Mpa
		Yield,23°C	ISO 527-2	-- Mpa

Electrical performance	Test Condition	Test Method	ASAHI JAPAN/13G25
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 0
Dielectric strength		IEC 60243-1	29 KV/mm
Dielectric strength			ASTM D149	29 KV/mm
Surface resistivity		ASTM D257	1E+15 ohms
Surface resistivity			IEC 60093	1E+15 ohms
Volume resistivity		ASTM D257	1E+15 ohms·cm
Volume resistivity		23°C	IEC 60093	1E+15 ohms·cm

Physical properties	Test Condition	Test Method	ASAHI JAPAN/13G25
Shrinkage rate	MD	Internal Method	0.50 %
		吸水率(Saturation,23°C)	Internal Method	-- %
		干	旭化成方法	0.5/0.9 %
		TD	Internal Method	0.90 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	-- %
Wear factor	湿	ASTM D-1044	12 ×10-6kg/1000times

impact performance	Test Condition	Test Method	ASAHI JAPAN/13G25
Impact strength of simply supported beam without notch		ISO 179	68 kJ/m²

flammability	Test Condition	Test Method	ASAHI JAPAN/13G25
UL flame retardant rating	0.75mm	UL 94	HB