ABS LNP™ FARADEX™ AS1003FR BK-038-5 SABIC INNOVATIVE US
202
- Unit Price:US$ 5,841 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:26.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Conductive
- Application Areas:Plastic bag｜Electronic and Electrical Applications
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 96.7 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 93.0 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 88.3 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 78.0 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.7E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 7.1E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 9.3E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 15.0 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 18 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 10to1.0E+3 ohms | |
| volume resistivity | ASTM D257 | 1E+04 ohms·cm | |
| Shielding effectiveness (EMI) | 3.00mm | 内部方法 | 50to65 dB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD:24小时 | ISO 294-4 | 0.27 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.20 % |
| shrinkage rate | MD：24小时 | ASTM D955 | 0.30 % |
| TD：24hr | ASTM D955 | 0.40 % | |
| TD:24小时 | ISO 294-4 | 0.39 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 6.2 % |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| flexural modulus | ASTM D790 | 3050 Mpa | |
| ISO 178 | 2800 Mpa | ||
| bending strength | ASTM D790 | 75.8 Mpa | |
| ISO 178 | 66.0 Mpa | ||
| Tensile modulus | ASTM D638 | 3160 Mpa | |
| ISO 527-2/1 | 2700 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 42.1 Mpa |
| 屈服 | ISO 527-2 | 38.0 Mpa | |
| 断裂 | ASTM D638 | 39.3 Mpa | |
| 断裂 | ISO 527-2 | 37.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 2.6 % |
| Tensile strain | 屈服 | ISO 527-2 | 2.2 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.