ABS AS1003FR BK-038-5 SABIC INNOVATIVE US
LNP™ FARADEX™
Plastic bag、Electronic and Electrical
Conductive
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/AS1003FR BK-038-5 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 18 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 15.0 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/AS1003FR BK-038-5 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+04 ohms·cm | |
| Surface Resistivity | ASTM D257 | 10to1.0E+3 ohms | |
| Shielding effectiveness (EMI) | 3.00mm | 内部方法 | 50to65 dB |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/AS1003FR BK-038-5 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2700 Mpa | |
| elongation | 屈服 | ASTM D638 | 2.6 % |
| bending strength | ASTM D790 | 75.8 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 2.2 % |
| tensile strength | 断裂 | ASTM D638 | 39.3 Mpa |
| 断裂 | ISO 527-2 | 37.0 Mpa | |
| Flexural modulus | ASTM D790 | 3050 Mpa | |
| Tensile modulus | ASTM D638 | 3160 Mpa | |
| elongation | 断裂 | ASTM D638 | 6.2 % |
| bending strength | ISO 178 | 66.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| Flexural modulus | ISO 178 | 2800 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 42.1 Mpa |
| 屈服 | ISO 527-2 | 38.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/AS1003FR BK-038-5 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.27 % |
| MD：24小时 | ASTM D955 | 0.30 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.20 % |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.40 % |
| TD:24小时 | ISO 294-4 | 0.39 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/AS1003FR BK-038-5 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 93.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 9.3E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 96.7 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.7E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 7.1E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 78.0 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 88.3 °C |