PA66

PA66 Leona™  13G43 001 ASAHI JAPAN

230
  • Unit Price:US$ 4,120 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    76MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Creep resistance｜Fatigue resistance｜high strength｜High rigidity｜Filler: Glass fiber reinforced material｜Enhanced strength and rigidity｜Glass fiber content is 43%｜43% filler by weight
  • Application Areas:Automotive sector｜component｜Engine hood parts｜Electronic field｜Electrical field｜Application in the automotive field｜Parts under the hood of a car｜Electrical/Electronic Applications｜Mechanical and electrical components｜Like a micro electric motor｜Automotive parts｜Like radiator water tank｜Gear lever
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 17984 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.75mmUL 94HB
Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate湿1.4 %
mechanical propertiesTest ConditionTest MethodTest Result
tensile strength干(湿)ASTM D-638196(157) Mpa
bending strength干(湿)ASTM D-790314(235) Mpa
Rockwell hardness干(湿)ASTM D-785118(-) R scale
flexural coefficient干(湿)ASTM D-79011.8(8.3) GPa
Elongation at Break干(湿)ASTM D-6383(4) %
Impact strength of cantilever beam gap干(湿)ASTM D-256127(206) J/m
Rockwell hardness干(湿)ASTM D-78596(80) M Scale
Tensile modulus23°CISO 527-212700 Mpa
tensile strengthASTM D638196 Mpa
Taber abraser1000CyclesASTM D1044-- mg
tensile strengthBreak,23°CISO 527-2207 Mpa
elongationBreakASTM D6383.0 %
Tensile strainBreak,23°CISO 527-23.0 %
Bending modulusASTM D79011800 Mpa
Bending modulus23°CISO 17811700 Mpa
bending strengthASTM D790314 Mpa
bending strength23°CISO 178303 Mpa
thermal performanceTest ConditionTest MethodTest Result
thermal conductivity0.40 W/m/K
Linear coefficient of thermal expansionMDASTM D6963E-05 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A255 °C
Hot deformation temperature1.82MPa,干ASTM D-648250 °C
Linear coefficient of thermal expansion干ASTM D-6963 ×10-5/K
Hot deformation temperature0.46MPa,干ASTM D-648260 °C
thermal conductivity干0.4 W/(m.K)
UL flame retardant rating干UL 94HB
Hot deformation temperature0.45MPa,UnannealedASTM D648260 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B260 °C
Hot deformation temperature1.8MPa,UnannealedASTM D648250 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rate干旭化成方法0.3/0.7 %
Wear factor湿ASTM D-104419 ×10-6kg/1000times
Shrinkage rateTDInternal Method0.70 %
Shrinkage rateMDInternal Method0.30 %
Shrinkage rate吸水率(Saturation,23°C)Internal Method-- %
Water absorption rateEquilibrium,23°C,50%RHISO 62-- %
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace index3.00mmIEC 60112PLC 0
Dielectric strengthIEC 60243-130 KV/mm
Dielectric strengthASTM D14930 KV/mm
Volume resistivity23°CIEC 600931E+15 ohms·cm
Volume resistivityASTM D2571E+15 ohms·cm
Surface resistivityIEC 600931E+15 ohms
Surface resistivityASTM D2571E+15 ohms
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM-SaleASTM D78596
Rockwell hardnessR-SaleASTM D785118
Rockwell hardnessM-SaleISO 2039-296
Rockwell hardnessR-SaleISO 2039-2118
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.