Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 13G43 001 ASAHI JAPAN
Leona™
Automotive sector、component、Engine hood parts、Electronic field、Electrical field、Application in the automo、Parts under the hood of a、Electrical/Electronic App、Mechanical and electrical、Like a micro electric mot、Automotive parts、Like radiator water tank、Gear lever
Creep resistance、Fatigue resistance、high strength、High rigidity、Filler: Glass fiber reinf、Enhanced strength and rig、Glass fiber content is 43、43% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 84 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 96 |
| R计秤 | ISO 2039-2 | 118 | |
| M计秤 | ISO 2039-2 | 96 | |
| R计秤 | ASTM D785 | 118 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| Water absorption rate | 湿 | 1.4 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 127(206) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 11.8(8.3) GPa |
| bending strength | ASTM D790 | 314 Mpa | |
| tensile strength | 干(湿) | ASTM D-638 | 196(157) Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 12700 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 207 Mpa |
| Flexural modulus | ASTM D790 | 11800 Mpa | |
| tensile strength | ASTM D638 | 196 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Rockwell hardness | 干(湿) | ASTM D-785 | 118(-) R scale |
| 干(湿) | ASTM D-785 | 96(80) M Scale | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| bending strength | 23°C | ISO 178 | 303 Mpa |
| 干(湿) | ASTM D-790 | 314(235) Mpa | |
| Flexural modulus | 23°C | ISO 178 | 11700 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 3(4) % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 0 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | ASTM D149 | 30 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| flammability | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.30 % |
| Wear factor | 湿 | ASTM D-1044 | 19 ×10-6kg/1000times |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| TD | 内部方法 | 0.70 % | |
| 干 | 旭化成方法 | 0.3/0.7 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/13G43 001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 250 °C |
| 1.82MPa,干，HDT | ASTM D-648 | 250 °C | |
| 0.45MPa,未退火，HDT | ASTM D648 | 260 °C | |
| thermal conductivity | 0.40 W/m/K | ||
| Heat distortion temperature | 0.46MPa,干，HDT | ASTM D-648 | 260 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C | |
| thermal conductivity | 干 | 0.4 W/(m.K) | |
| UL flame retardant rating | 干 | UL 94 | HB |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 255 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 cm/cm/°C |
| 干 | ASTM D-696 | 3 ×10-5/K |