PA6 AKROMID® B3GK50 AKRO-PLASTIC GERMANY

360

Unit Price:US$ 2,740 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass beads｜50% filler by weight
Application Areas:furniture｜Shell｜Application in the automotive field｜Electrical/Electronic Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	32 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	42 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	FMVSS302	<100 mm/min
UL flame retardant rating	1.6mm	UL 94	HB
Burning wire flammability index	1.6mm	IEC 60695-2-12	650 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	5700 Mpa
tensile strength	Break	ISO 527-2/5	75.0 Mpa
Tensile strain	Break	ISO 527-2/5	4.0 %
Bending modulus		ISO 178	5200 Mpa
bending strength		ISO 178	135 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	188 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	75.0 °C
Melting temperature		DIN EN11357-1	225 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.0 %
Water absorption rate	Saturation,23°C	ISO 62	4.7 %
Hygroscopicity	70°C，62%RH	ISO 1110	1.5 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+13 ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Compared to the anti leakage trace index	SolutionA	IEC 60112	V

Supplementary Information	Test Condition	Test Method	Test Result
ReinforcementContent		ISO 1172	50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.