PA6 B3GK50 AKRO-PLASTIC GERMANY
AKROMID®
furniture、Shell、Application in the automo、Electrical/Electronic App
Filler: Glass beads、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GK50 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 42 kJ/m² |
| -30°C | ISO179/1eU | 32 kJ/m² |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GK50 |
|---|---|---|---|
| ReinforcementContent | ISO1172 | 50 % |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GK50 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/5 | 75.0 Mpa |
| Tensile modulus | ISO527-2/1 | 5700 Mpa | |
| Tensile strain | 断裂 | ISO527-2/5 | 4.0 % |
| Bending modulus 2 | ISO178 | 5200 Mpa | |
| Bending stress 2 | ISO178 | 135 Mpa |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GK50 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+13 ohms | |
| CTI | 解决方案A | IEC60112 | 500 V |
| Volume resistivity | IEC60093 | 1E+15 ohms·cm |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GK50 |
|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| GlowWireFlammability Index | 1.6mm | IEC60695-2-12 | 650 °C |
| Burning rate 4 | 1.00mm | FMVSS302 | <100 mm/min |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GK50 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.1 % |
| Water absorption rate | 饱和,23°C | ISO62 | 4.7 % |
| HumidityAbsorption-62%RH | 70°C | ISO1110 | 1.5 % |
| Shrinkage rate | MD | ISO294-4 | 1.0 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GK50 |
|---|---|---|---|
| 0.45MPa,未退火 | ISO75-2/B | 188 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 75.0 °C | |
| Melting temperature 5 | DINEN11357-1 | 225 °C |