Material Description
- Material Properties:Flame retardant｜UV resistance
- Application Areas:Flame retardant｜UV resistance
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 70 |
| R 级 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 132 °C | |
| vicat | -- | ASTM D15257 | 154 °C |
| -- | ISO 306/B120 | 145 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | -40 到 95°C，流动 | ASTM E831 | 6.8E-5 cm/cm/°C |
| specific heat | ASTM C351 | 1260 J/kg/°C | |
| thermal conductivity | ASTM C177 | 0.29 W/m/K | |
| RTI Elec | UL 746 | 80.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.817mm | UL 94 | V-2 |
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 750 °C |
| 1.5 mm | IEC 60695-2-12 | 850 °C | |
| Hot filament ignition temperature | 0.75 mm9 | IEC 60695-2-13 | 875 °C |
| 1.5 mm | IEC 60695-2-13 | 850 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Dart impact | 23°C | ASTM D3029 | 169 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 7.0 g/10 min |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 7.00 cm3/10min |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.15 % |
| 平衡, 23°C | ASTM D570 | 0.35 % | |
| 平衡, 100°C | ASTM D570 | 0.58 % | |
| Outdoor applicability | UL 746C | f2 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | > 1.0E+17 ohms·cm | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 15 KV/mm |
| dielectric constant | 60 Hz | ASTM D150 | 3.17 |
| 50 kHz | ASTM D150 | 3.17 | |
| 1 MHz | ASTM D150 | 2.96 | |
| Dissipation Factor | 50 Hz | ASTM D150 | 9.0E-4 |
| 60 Hz | ASTM D150 | 9.0E-4 | |
| 1 MHz | ASTM D150 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 290 to 310 °C | ||
| Temperature in the middle of the barrel | 300 to 320 °C | ||
| Temperature at the front of the material cylinder | 310 to 330 °C | ||
| Spray nozzle temperature | 305 to 325 °C | ||
| Processing (melt) temperature | 310 to 330 °C | ||
| mold temperature | 80 to 115 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| tensile strength | 屈服2 | ASTM D638 | 62.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| 断裂2 | ASTM D638 | 65.0 Mpa | |
| 断裂 | ISO 527-2/50 | 63.0 Mpa | |
| elongation | 屈服2 | ASTM D638 | 7.0 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 断裂2 | ASTM D638 | 110 % | |
| flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 2340 Mpa |
| --4 | ISO 178 | 2300 Mpa | |
| bending strength | --4,5 | ISO 178 | 94.0 Mpa |
| 屈服, 50.0 mm 跨距3 | ASTM D790 | 93.0 Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.