PBT

PBT SCHULADUR® A GB 20 A SCHULMAN USA

343

Unit Price:US$ 3,994 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.60mm
UL flame retardant rating	UL flame retardant rating		UL -94	HB 3.20mm
Ignition temperature of heating wire	1.50mm	IEC 60695-2-12	725 °C
Ignition temperature of heating wire	Ignition temperature of heating wire	3.00mm	IEC 60695-2-12	725 °C
Relative temperature of heating wire	1.50mm	IEC 60695-2-13	750 °C
Relative temperature of heating wire	Relative temperature of heating wire	3.00mm	IEC 60695-2-13	750 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	50 Mpa
Elongation at Break	23°C	ISO 527-2	6.00 %
Tensile modulus	23°C	ISO 527-2	3400 Mpa
bending strength	23°C	ISO 178	83 Mpa
Bending modulus	23°C	ISO 178	3300 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.5 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	30 kJ/m²

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	94 °C
Vicat softening temperature		ISO 306/A50	218 °C
Vicat softening temperature	Vicat softening temperature		ISO 306/B50	184 °C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	175 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250℃/2.16Kg	ISO 1133	15.0 cm3/10min

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	113 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT SCHULADUR® A GB 20 A SCHULMAN USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet