PPA

PPA LNP™ LUBRICOMP™ UCL-4536 HS SABIC INNOVATIVE US

279

Unit Price:US$ 7,741 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
24MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Flame retardant｜Filler: Carbon fiber reinforced material｜30% filler by weight
Application Areas:Automotive components｜Electronic and electrical accessories
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.2 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	36 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	5.60 J
Multi axis Instrumented Impact Energy		ISO 6603-2	1.92 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break,50.0mmSpan	ASTM D790	326 Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.35
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.32
Wear factor	Ring	ASTM D3702Modified	0.550 10^-10in^5-min/ft-lb-hr
Wear factor	Wear factor	Washer	ASTM D3702Modified	14.0 10^-10in^5-min/ft-lb-hr
Tensile modulus		ASTM D638	26400 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	26100 Mpa
tensile strength	Break	ASTM D638	235 Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	229 Mpa
elongation	Break	ASTM D638	1.3 %
Tensile strain	Break	ISO 527-2/5	1.2 %
Bending modulus	50.0mmSpan	ASTM D790	22400 Mpa
Bending modulus	Bending modulus		ISO 178	22200 Mpa
bending strength		ISO 178	321 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	278 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	280 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	259 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	260 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：24hr	ASTM D955	0.11 %
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	0.72 %
Water absorption rate	24hr,50%RH	ASTM D570	0.26 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.40 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPA LNP™ LUBRICOMP™ UCL-4536 HS SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet